Structure and Mechanical Properties of Ni��P��Nano Al2O3 Composite Coatings Synthesized by Electroless Plating |
ZHOU Guang��hong1,DING Hong��yan1,2,ZHOU Fei2,ZHANG Yue1 |
1. Department of Mechanical Engineering, Huaiyin Institute of Technology, Huai��an 223001, Jiangsu, China; 2. Institute of Bio��inspired Structure and Surface Engineering, Academy of Frontier Science, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, Jiangsu, China |
|
|
Abstract Ni��P��nano Al2O3 composite coatings were deposited by electroless plating, and their microstructures were observed by SEM (scanning electron microscope). The microhardness and the wear resistance of the Ni��P��nano Al2O3 composite coatings were measured using microhardness tester and block��on��ring tribometer, respectively, and the comparison with those of Ni��P coatings or Ni��P��micro Al2O3 coating was given. The influences of aging temperature on their hardness and wear resistance were analyzed. The results showed that the nano Al2O3 particles were distributed uniformly in the Ni��P��Al2O3 coatings. Among three kinds of Ni��P based coatings, the hardness and wear resistance of Ni��P��nano Al2O3 coatings were largest, and the maximum values could be obtained at 400 ��. This indicated that the precipitation of nano Al2O3 particles would improve the hardness and wear resistance of the Ni��P coatings.
|
Received: 01 January 1900
|
|
|
|
[1] |
Xiao-li Zhao,,Yong-jian Zhang,Cheng-wei Shao,Wei-jun Hui,Han Dong. Thermal stability of retained austenite and mechanical properties of medium-Mn steel during tempering treatment[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 830-837. |
[2] |
Hong-ru Ren,Jin-tao Gao,Zhe Wang,Chong Li,Fu-qiang Wang,Zhan-cheng Guo. Evolution of microstructure, mechanical and magnetic properties of electrodeposited 50%Ni-Fe alloy foil after thermal treatment[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 844-851. |
[3] |
Reng-chong Xu,,Yan-lin He,,Hu Jiang,,Hua Wang,,Na-qiong Zhu,,Xiao-gang Lu,, Lin Li,. Microstructures and mechanical properties of ferrite-based lightweight steel with different compositions[J]. Chinese Journal of Iron and Steel, 2017, 24(7): 737-742. |
[4] |
Yong-xing Jiao,Jian-sheng Liu*,Xing-wang Duan,Xiao-hua Zheng,Wen-wu He. Prediction of critical forging penetration efficiency for 06Cr19Ni9NbN steel by dynamic recrystallization[J]. Chinese Journal of Iron and Steel, 2017, 24(6): 649-653. |
[5] |
Ming-bo Zhou,Jing-lin Tang,*,Jie Yang,Cun-yu Wang. Tailored properties of a novelly-designed press-hardened 22MnMoB steel[J]. Chinese Journal of Iron and Steel, 2017, 24(5): 508-512. |
[6] |
Zhong-liang Tian,,Sen-bao Jiang,Zheng-zong Chen,Han-sheng Bao,Zheng-dong Liu,*. Microstructural evolution and mechanical properties of a new Ni-based heat-resistant alloy during aging at 750��C[J]. Chinese Journal of Iron and Steel, 2017, 24(5): 513-519. |
|
|
|
|