Preparation of Nanocrystalline 430L Stainless Steel by HEBM and SPS |
NI Hong��wei1,HE Hang2,LI Guang��qiang1,LIU Jing1 |
1. Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan 430081, Hubei, China;2. Xiangtan Iron and Steel Group Co Ltd, Xiangtan 411100, Hunan, China |
|
|
Abstract Preparation of nanocrystalline 430L stainless steel by both high��energy ball milling and spark plasma sintering technique has been investigated. The results have shown that the hardness can be improved markedly with an increase in sintering temperature and holding time. The lower the apparent porosity of nanocrystalline 430L stainless steel, the higher is the Vickers��hardness. The tensile strength reached a maximum value of 713 MPa when the sample was sintered at 1 173 K for 10 min, and then it evidently decreased with an increase in sintering temperature and holding time because of the growth of crystalline grain.
|
Received: 01 January 1900
|
|
|
|
[1] |
Wen-juan Ge,Xu-ting Li,Peng Li,Peng-chao Qiao,Jian-wei Du,Shuai Xu,Yan Wang*. Microstructures and properties of CuZrAl and CuZrAlTi medium entropy alloys prepared by mechanical alloying and spark plasma sintering[J]. Chinese Journal of Iron and Steel, 2017, 24(4): 448-454. |
[2] |
Bao-chao ZHENG,Zhi-fu HUANG,Jian-dong XING,Yi-yang XIAO,Xiao FAN,Yong WANG. Effects of Chromium Addition on Preparation and Properties of Bulk Cementite[J]. Chinese Journal of Iron and Steel, 2016, 23(8): 842-850. |
[3] |
Hui LI,Yong-feng LIANG,Feng YE. Evolution of Microstructure and Ordering in Rolling Process of Fe-6.5 mass% Si Alloy[J]. Chinese Journal of Iron and Steel, 2016, 23(5): 453-458. |
[4] |
Xiao-ping DONG,Yan-rong PANG,Li-ying YANG,Qing WANG,Zhi-yuan LI. Effect of Spark Plasma Sintering Temperature on Electrochemical Properties of La0.82Mg0.18Ni3.50Co0.15 Alloy[J]. Chinese Journal of Iron and Steel, 2016, 23(5): 459-465. |
[5] |
Ying-ying YUE,Cheng-jun LIU,Pei-yang SHI,Mao-fa JIANG,Li-yan QIN,Guang-wei FAN. Descaling Behavior of 430 Hot-rolled Stainless Steel in HCl-based Solution[J]. Chinese Journal of Iron and Steel, 2016, 23(3): 190-196. |
[6] |
Fei GAO,Fu-xiao YU,Hai-tao LIU,Zhen-yu LIU. Hot Deformation Behavior and Flow Stress Prediction of Ultra Purified 17% Cr Ferritic Stainless Steel Stabilized with Nb and Ti[J]. Chinese Journal of Iron and Steel, 2015, 22(9): 827-836. |
|
|
|
|