Thermal Stability of Retained Austenite in TRIP Steel After Different Treatments |
SHI Wen1,LI Lin1,Bruno C De Cooman2,Patrick Wollants3,YANG Chun��xia1 |
1. Department of Material Science and Engineering, Shanghai University, Shanghai 200072, China;2. Laboratory for Iron and Steel Making, Department of Material Science and Engineering, Technologiepark 903 BE��9052, Ghent, Belgium; 3. Department MTM, KU Leuven, Heverlee B��3001, Belgium |
|
|
Abstract Thermal decomposition of retained austenite in TRIP steel was investigated by means of differential scanning calorimetry (DSC). The decomposition curve was abnormal, and the decomposition temperature and the activation energy were measured by the Kissinger method, which were all higher than those in quenched steel. The thermal decomposition data of samples soaked in liquid nitrogen after TRIP treatment were all similar to those without additional low temperature treatment. It indicated that there is a high thermal stability in retained austenite of the TRIP steel at low temperature, which was also proved by XRD analysis.
|
Received: 01 January 1900
|
|
|
|
[1] |
Xiao-li Zhao,,Yong-jian Zhang,Cheng-wei Shao,Wei-jun Hui,Han Dong. Thermal stability of retained austenite and mechanical properties of medium-Mn steel during tempering treatment[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 830-837. |
[2] |
Hui Guo,Peng Zhou,*,Ai-min Zhao,,Chao Zhi,Ran Ding,Jia-xing Wang. Effects of Mn and Cr contents on microstructures and mechanical properties of low temperature bainitic steel[J]. Chinese Journal of Iron and Steel, 2017, 24(3): 290-295. |
[3] |
Ji-bo Peng,,Hu Jiang,,Gong-ting Zhang,Li-ben Chen,,Na-qiong Zhu,,Yan-lin He,,*, Xiao-gang Lu,,Lin Li,. In-situ analysis of retained austenite transformation in high-performance micro-alloyed TRIP steel[J]. Chinese Journal of Iron and Steel, 2017, 24(3): 313-320. |
[4] |
Sajad Gholami SHIRI,Seyed Ahmad Jenabali JAHROMI,Yahya PALIZDAR,Majid BELBASI. Unexpected Effect of Nb Addition as a Microalloying Element on Mechanical Properties of �Ī�TRIP Steels[J]. Chinese Journal of Iron and Steel, 2016, 23(9): 988-996. |
[5] |
Wu- hua YUAN,Xue- hui GONG,,Yong- qing SUN,Jian- xiong LIANG. Microstructure Evolution and Precipitation Behavior of 0Cr16Ni5Mo Martensitic Stainless Steel during Tempering Process[J]. Chinese Journal of Iron and Steel, 2016, 23(4): 401-408. |
[6] |
Shi-meng ZHOU,,Xing-wang CHENG,,You-jing ZHANG,,Meng WANG,,Wen JIANG,,Hong-nian CAI,. Factors Affecting the Mechanical Properties of Ultra-high-strength Bainitic Steel Containing W and 0.33 mass% C[J]. Chinese Journal of Iron and Steel, 2016, 23(3): 289-296. |
|
|
|
|