Austenitization Behaviors of X80 Pipeline Steels With High Nb and Micro-Ti Treatment |
LIU Qing-you SUN Xin-jun JIA Shu-jun ZHANG Lu-lin HUANG Guo-jian REN Yi |
|
|
Abstract The austenitization behaviors of two high Nb-containing X80 pipeline steels with different Ti contents, including the dissolution of microalloying precipitates and the austenite grain growth behaviors, were investigated by using physical-chemical phase analysis method and optimal microstructure observation. The results illustrate that most Nb can be dissolved into austenite during the soaking at 1180��, but very little amount of Ti can be dissolved. It is found that during soaking, the austenite grain growth rate is initially high, and then it decreases after 1h soaking; moreover, the austenite grains grow up more rapidly at temperatures above 1180�� than at temperatures below 1180��. It is shown that the steel with 0.016%Ti content has a larger austenite grain size than the steel with 0.012%Ti under the same soaking conditions, which has been explained by considering the particle size distribution.
|
Received: 28 August 2008
|
|
|
|
[1] |
Ying Ci,*,Zhan-zhan Zhang. Simulation study on heat-affected zone of high-strain X80 pipeline steel[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 966-973. |
[2] |
Ze-an Lv,,Hong-wei Ni,,*,Hua Zhang,,Cheng-song Liu,,**. Evolution of MnS inclusions in Ti-bearing X80 pipeline steel[J]. Chinese Journal of Iron and Steel, 2017, 24(6): 654-660. |
[3] |
Li-wei WANG,,Xiao-gang LI,Cui-wei DU,Peng ZHANG,Yi-zhong HUANG. In-situ Corrosion Characterization of API X80 Steel and Its Corresponding HAZ Microstructures in an Acidic Environment[J]. Chinese Journal of Iron and Steel, 2015, 22(2): 135-144. |
[4] |
KONG De-jun,WU Yong-zhong,LONG Dan. Stress Corrosion of X80 Pipeline Steel Welded Joints by Slow Strain Test in NACE H2S Solutions[J]. Chinese Journal of Iron and Steel, 2013, 20(1): 40-46. |
|
|
|
|