| Recrystallization of a Single Crystal Nickel-Base Superalloy |
| ZHANG Bing,TAO Chun-hu,LU Xin,LIU Chang-kui,HU Chun-yan,BAI Ming-yuan |
|
|
|
|
Abstract A series of experiments of investigating the recrystallization of single crystal DD3 superalloy were carried out. The threshold temperature for recrystallization and the effect of annealing temperature on recrystallization were studied. The results show that the threshold temperature for recrystallization of the shot��peened DD3 samples is between 1 000 �� and 1 050 �� under the condition of annealing for 2 h, and the recrystallization depth increases with the rise of the annealing temperature. Below 1 150 ��, the recrystallization depth increases slowly with the temperature climbing, while above 1 150 ��, the recrystallization depth increases quickly with the rise of the temperature. The solution of the �á� phase is a critical factor of the recrystallization behavior of DD3 superalloy. In addition, the kinetics and microstructural evolution of recrystallization at 1 200 �� were also studied. It is found that the recrystallization progresses rapidly at 1 200 �� through the growth of fully developed recrystallized grains, and the recrystallization process on the shot��peened surface is similar to that of wrought materials, including nucleation of recrystallization, growth of new grains into the matrix, and growth of new grains by swallowing up each other.
|
|
Received: 07 November 2008
|
|
|
|
| [1] |
Zong-ye Ding,Di Zhang,Qiao-dan Hu,,*,Long Zeng,Jian-guo Li,. Constitutive analysis and optimization on hot working parameters of as-cast high Cr ultra-super-critical rotor steel with columnar grains[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 916-924. |
| [2] |
Yong-xing Jiao,Jian-sheng Liu*,Xing-wang Duan,Xiao-hua Zheng,Wen-wu He. Prediction of critical forging penetration efficiency for 06Cr19Ni9NbN steel by dynamic recrystallization[J]. Chinese Journal of Iron and Steel, 2017, 24(6): 649-653. |
| [3] |
Peng Zhou,,Qing-xian Ma,,*. Static recrystallization behavior of 25CrMo4 mirror plate steel during two-pass hot deformation[J]. Chinese Journal of Iron and Steel, 2017, 24(2): 222-228. |
| [4] |
Zhen-xue Shi,Shi-zhong Liu,Xiao-dai Yue,Li-jie Hu,Wan-peng Yang,Xiao-guang Wang,Jia-rong Li. Effect of cellular recrystallization on tensile properties of a nickel-based single crystal superalloy containing Re and Ru[J]. Chinese Journal of Iron and Steel, 2017, 24(10): 1059-1064. |
| [5] |
Dong-dong Zhuang,*,Lei-gang Wang,Yao Huang,Xiao-min Li,Hua-yang Zhang,De-wei Ren. Microstructure and texture evolution during recrystallization of low-carbon steel sheets[J]. Chinese Journal of Iron and Steel, 2017, 24(1): 84-90. |
| [6] |
Wu-xin ZHAO,Yuan WU,Sui-he JIANG,Hui WANG,Xiong-jun LIU,Zhao-ping LU. Micro-alloying Effects of Yttrium on Recrystallization Behavior of an Alumina-forming Austenitic Stainless Steel[J]. Chinese Journal of Iron and Steel, 2016, 23(6): 553-558. |
|
|
|
|
2009, Vol. 16 