| Evolution and Coarsening of Carbides in 2.25Cr-1Mo Steel Weld Metal During High Temperature Tempering |
TAO Peng, ZHANG Chi, YANG Zhi-gang, et al |
|
|
|
|
Abstract Transformation and coarsening of carbides in 2.25Cr-1Mo steel weld metal during tempering at 700 oC for different time intervals ranging from 1 to 150 h has been examined by transmission electron microscopy and scanning electron microscopy. M3C carbides were observed in the as-welded specimens and when tempered the precipitates were mainly composed of M3C, M7C3 and M23C6 carbides. A sequence for corresponding carbide transformation during tempering with initial precipitation of M3C and followed by M7C3 and M23C6 has been proposed. The precipitation of M7C3 with higher Cr content is the main factor contributing to the decrease of coarsening rate of precipitates after prolonged tempering. The decrease of hardness in the tempered specimens agreed well with the prediction of the weakening of precipitation strengthening due to the coarsening of carbides.
|
|
Received: 05 January 2009
|
|
|
|
| [1] |
Yang Yun,Qing-wu Cai,,Bao-sheng Xie,*,Shuang Li. Effect of tempering temperature on strain hardening exponent and flow stress curve of 1000 MPa grade steel for construction machinery[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 950-956. |
| [2] |
Xiao-li Zhao,,Yong-jian Zhang,Cheng-wei Shao,Wei-jun Hui,Han Dong. Thermal stability of retained austenite and mechanical properties of medium-Mn steel during tempering treatment[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 830-837. |
| [3] |
Xu Yang,,Bo Liao,Fu-ren Xiao,Wei Yan,Yi-yin Shan,Ke Yang. Ripening behavior of M23C6 carbides in P92 steel during aging at 800��C[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 858-864. |
| [4] |
Reng-chong Xu,,Yan-lin He,,Hu Jiang,,Hua Wang,,Na-qiong Zhu,,Xiao-gang Lu,, Lin Li,. Microstructures and mechanical properties of ferrite-based lightweight steel with different compositions[J]. Chinese Journal of Iron and Steel, 2017, 24(7): 737-742. |
| [5] |
Shi-lu Zhao,*,Zhen Zhang,Jun Zhang,Jian-ming Wang,Zheng-gui Zhang,Shuang-hong Wang. High temperature oxidation resistance of CrN/(Ti,Al,Zr,Cr)N bilayer films deposited by multi-arc ion plating[J]. Chinese Journal of Iron and Steel, 2017, 24(3): 343-349. |
| [6] |
Hai-feng Xu,,*,Feng Yu,Chang Wang,Wan-li Zhang,Jian Li,Wen-quan Cao. Comparison of microstructure and property of high chromium bearing steel with and without nitrogen addition[J]. Chinese Journal of Iron and Steel, 2017, 24(2): 206-213. |
|
|
|
|
2010, Vol. 17 