Nonequilibrium Grain Boundary Segregation of Phosphorus in Ni-Cr-Fe Superalloy |
WANG Kai, SI Hong, YANG Chun, XU Ting��dong |
|
|
Abstract In virtue of Auger electron spectroscopy, the grain-boundary concentrations of phosphorus in Ni-Cr-Fe superalloy after solution-treated at 1180�� for 45 min are measured, the results show that a peak of phosphorus concentration occurs at about 180 min during isothermal ageing at 500��, and a maximum concentration of phosphorus appears also at about 500�� for all specimens aged for 20 min at temperatures of 200,400,500,700 and 800��. The results are analysed with the laws of non-equilibrium grain-boundary segregation. It is found from the analysis that peaks are relative to critical time for non-equilibrium grain-boundary segregation of phosphorus.
|
Received: 16 December 2009
|
|
|
|
[1] |
Wei Wu,*,Shi-fan Dai,Yue Liu. Dephosphorization stability of hot metal by double slag operation in basic oxygen furnace[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 908-915. |
[2] |
Dong��bo HUANG,Yan��bing ZONG,Ru��fei WEI,Wei GAO,Xiao��ming LIU,. Direct Reduction of High��phosphorus Oolitic Hematite Ore Based on Biomass Pyrolysis[J]. Chinese Journal of Iron and Steel, 2016, 23(9): 874-883. |
[3] |
De-qing ZHU,Hao WANG,Jian PAN,Cong-cong YANG. Influence of Mechanical Activation on Acid Leaching Dephosphorization of High-phosphorus Iron Ore Concentrates[J]. Chinese Journal of Iron and Steel, 2016, 23(7): 661-668. |
[4] |
Wei WU,Jian-jun GAO,Jia-qing ZENG,Yuan-hong QI,Jian-chang WANG,Xi-dong ZHANG. Reduction of Carbon-bearing Pellets of Oolitic Hematite in a Shaft Furnace[J]. Chinese Journal of Iron and Steel, 2016, 23(3): 210-219. |
[5] |
Hui-qing TANG,Yan-qi QIN,Teng-fei QI,Zhi-lei DONG,Qing-guo XUE. Application of Wood Char in Processing Oolitic High-phosphorus Hematite for Phosphorus Removal[J]. Chinese Journal of Iron and Steel, 2016, 23(2): 109-115. |
[6] |
Jian-chao LI,Qing L�u,Xiao-jie LIU,Shu-hui ZHANG,Dong-hui LIU. Phosphorus Capacity of CaO-SiO2-Al2O3-MgO-FexO Slag[J]. Chinese Journal of Iron and Steel, 2015, 22(5): 377-381. |
|
|
|
|