Effect of Laser Power on the Cladding Temperature Field and the Heat Affected Zone |
LUO Fang, YAO Jian��hua, HU Xia��xia, CHAI Guo��zhong |
|
|
Abstract Abstract: In this paper, H13 powder is cladded on P20 base during continuous CO2 laser, the influence of processing technologies such as the laser power is analyzed. The 3-D model of synchronous powder feeding is established under Gauss heat source, the simulation results are compared with the experimental data. The results show that the temperature field and the size of heat affected zone are affected by laser power. In the heat affected zone, experimental sizes are compared with simulative sizes, the average errors in width and in depth are 15% and 4.5%, respectively.
|
Received: 24 November 2009
|
Corresponding Authors:
LUO Fang
|
|
|
|
[1] |
LI Jun��ZHANG Ling-ling��ZHAO Gui-zhou��CANG Da-qiang. Pilot practice of direct modification of molten blast furnace slag and preparation of mineral wool fiber[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 99-103. |
[2] |
XU Ren-ze��ZHANG Jian-liang��ZHANG He-shun��LIU Chang-jiang�� FAN Xiao-yue��WANG Zhi-yu. Influence of TiO2 on properties of Jingtang blast furnace slag and thermodynamic analysis[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 104-108. |
[3] |
JIANG Zhou-hua��ZHANG Xin-fa��LIU Fu-bin��GONG Wei. Harmful impurities control of raw material used in Ni-based superalloy production[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 1-10. |
[4] |
SONG Guang-yi��YANG Quan��WANG Xiao-chen��ZHANG Xi-bang�� WANG Feng-mei��WANG Qiu-na. Work roll wear law for hot strip temper mill[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 54-59. |
[5] |
WANG Bing-xing��XIONG Lei��ZHANG Tian��WANG Zhao-dong��WANG Guo-dong. Influence on deformation permeability of plate by controlled rolling process with inter-pass water cooling technology[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 60-65. |
[6] |
YU Hui��ZHAI Jian-wei��ZHANG Chao-fan��LIU Shuai-shuai��LIU Li-gang. Microstructures and properties of nuclear carbon manganese steels P280GH after accelerated aging[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 66-72. |
|
|
|
|