Physical Properties and Regulating Mechanism of Fluoride��Free and Harmless B2O3��Containing Mould Flux |
LI Gui��rong,WANG Hong��ming,DAI Qi��xun,ZHAO Yu��tao,LI Jing��sheng |
School of Materials Science and Engineering, Jiangsu University, Zhenjiang 212013, Jiangsu, China |
|
|
Abstract The flux agents in common mould fluxes were fluoride and sodium oxide, which would do great harm to environments. B2O3 was selected as flux. The physical properties of B2O3��containing mould fluxes were studied. The corresponding physical properties of 37��91%CaO��43��09%SiO2��5%Al2O3��5%MgO��2%Li2O��7%B2O3 mould fluxes were as follows: the melting point was 909 ��, the flowing temperature was 1 160 ��, the viscosity and surface tension at 1 300 �� were 0��4 Pa��s and 0��32 N/m respectively, which could meet the demands for certain kinds of steels for mould fluxes in continuous casting.
|
Received: 01 January 1900
|
|
|
|
[1] |
Hua��qiang HAO,,Yu��zhu ZHANG,,Su��ju HAO,Chao��fa ZHANG,Wu��feng JIANG,Peng��hui CUI. Preparation and Metallurgical Analysis of High Activity Burnt Lime for Steelmaking[J]. Chinese Journal of Iron and Steel, 2016, 23(9): 884-890. |
[2] |
Di WU,,Wan-tang FU,Yong LI,Chun-xu WANG,Jing-lin TANG. Phase Stability, Elastic, Thermo-physical and Electronic Properties of Hexa-(Mo,Cr,W)2C from First-principles Calculations[J]. Chinese Journal of Iron and Steel, 2016, 23(10): 1096-1103. |
|
|
|
|