| Effect of Thermomechanical Treatment Temperature on Structure and Properties of CFB/M Ultra-High Strength Steel |
XU Xue-xia,BAI Bing-zhe |
|
|
|
|
Abstract Modified CCT diagram of carbide free bainite-martensite��CFB/M��high strength steel was established applying small sample control cooling. In addition, the influence of thermomechanical treatment temperature on its structure and properties was discussed. The experimental results show that when deformed at 860oC and below, ferrite transformation occurred due to strain, and with the decrease of ausforming temperature, the quantity of ferrite increased and strength and toughness deteriorate. Therefore, certain information were provided for drawing technical parameter of ausforming process; firstly, the thermomechanical treatment temperature shouldn��t be above 860oC to avoid ferrite formation induced by deformation; secondly, cooling rate shouldn��t be too slow to avoid ferrite precipitating during cooling process after ausforming process.
|
|
Received: 22 December 2008
|
|
Corresponding Authors:
Xue-xia Xu
|
|
|
|
| [1] |
Qiu-lin Niu,,Wei-wei Ming,Ming Chen,Si-wen Tang,,Peng-nan Li,. Dynamic mechanical behavior of ultra-high strength steel 30CrMnSiNi2A at high strain rates and elevated temperatures[J]. Chinese Journal of Iron and Steel, 2017, 24(7): 724-729. |
| [2] |
Meng-xuan Guo,Kai-xiang Gao,Wu-rong Wang,Xi-cheng Wei. Microstructural evolution of Al-Si coating and its influence on high tempera-ture tribological behavior of ultra-high strength steel against H13 steel[J]. Chinese Journal of Iron and Steel, 2017, 24(10): 1048-1058. |
| [3] |
Juan JIA,Wei-wei ZHU,Xin-li SONG,Ze-xi YUAN. Precipitation Behavior of FeTiP in Ti-added Interstitial Free High Strength Steels[J]. Chinese Journal of Iron and Steel, 2016, 23(7): 692-698. |
| [4] |
Xiang-dong HUO,Lie-jun LI,Zheng-wu PENG,Song-jun CHEN. Effects of TMCP Schedule on Precipitation, Microstructure and Properties of Ti-microalloyed High Strength Steel[J]. Chinese Journal of Iron and Steel, 2016, 23(6): 593-601. |
| [5] |
Biao JU,Hui-bin WU,Di TANG,Ning DANG. Characterization of (Nb,Ti,Mo)C Precipitates in an Ultrahigh Strength Martensitic Steel[J]. Chinese Journal of Iron and Steel, 2016, 23(5): 495-500. |
| [6] |
Fan ZHEN,Kuan ZHANG,Zhi-long GUO,Jin-bo QU. Effect of Martensite Fine Structure on Mechanical Properties of an 1100 MPa Grade Ultra-high Strength Steel[J]. Chinese Journal of Iron and Steel, 2015, 22(7): 645-651. |
|
|
|
|
2010, Vol. 17 