| Numerical Simulation of Influence of Casting Speed Variation on Surface Fluctuation of the Molten Steel in Mold |
| ZHANG Qiao-ying, WANG Xin-hua |
|
|
|
|
Abstract The influences of casting speed variation on surface fluctuation of the molten steel of mold during continuous casting were investigated with numerical simulation method. It was found that, when the casting speed was evenly decreased from 1.4m/min to 0.6m/min, increases of the surface fluctuation of the molten steel of mold were observed only on time that was at the start of casting speed change. While, in experiment of increasing casting speed evenly from 0.6m/min to 1.4m/min, increases of the surface fluctuation of the molten steel of mold were observed only at the time when the casting speed was stopped to increase after it had been increased to 1.4m/min. For surface fluctuation of the molten steel of mold which was produced during the casting speed evenly increasing or decreasing period and at the time when increasing or decreasing the casting speed at low casting speed level (0.6m/min), the influence of casting speed change was very small. In addition, it was found that, at high casting speed level (1.4m/min), even a little change of casting speed could result in remarkable increase of the surface fluctuation. Thus, at high casting speed, changing casting speed should be avoided or using much slower speed changing rate.
|
|
Received: 06 July 2009
|
|
|
|
| [1] |
Da-shan Sui,*,Hai-ming Zhang,Hong-yang Zhu,Zhe Zhu,Zhen-shan Cui. Effects of process parameters on fragment and refinement of millimeter-grade coarse grains for 316LN steel during hot cogging[J]. Chinese Journal of Iron and Steel, 2017, 24(5): 529-535. |
| [2] |
Chao Zhou,,Xing-zhong Zhang,*,Fang Wang,Ping-fei Liu,Yi-ming Fang. Mechanism analysis of non-sinusoidal oscillation of continuous casting mold synchronously driven by double servomotors[J]. Chinese Journal of Iron and Steel, 2017, 24(3): 251-257. |
| [3] |
Yang Liu,Xin-hua Liu*,Hua-dong Fu,Min-xuan Lou,Jian-xin Xie. Effects of process parameters on surface quality, composition segregation, microstructure and properties of QSn6.5-0.1 alloy slabs fabricated by HCCM horizontal continuous casting[J]. Chinese Journal of Iron and Steel, 2017, 24(3): 273-281. |
| [4] |
Yonghui PARK,Hyunchul PARK. Dynamic Response of Mold Oscillator Interacting with Steel Slabs[J]. Chinese Journal of Iron and Steel, 2016, 23(9): 900-909. |
| [5] |
Zheng-wei GU,,Meng-meng L��,,Xin LI,,Hong XU,. Stretch Bending of Z-section Stainless Steel Profile[J]. Chinese Journal of Iron and Steel, 2016, 23(6): 525-530. |
| [6] |
Cun-jiang TANG,Shi-long LIU,Cheng-jia SHANG. Micromechanical Behavior and Failure Mechanism of F/B Multi-phase High Performance Steel[J]. Chinese Journal of Iron and Steel, 2016, 23(5): 489-494. |
|
|
|
|
2010, Vol. 17 