| Influence of Lanthanum Ion��Implantation on Adhesive Property of Oxide Film Formed on Co��40Cr Alloy |
| JIN Hui��ming1,ZHANG Lin��nan2,LIU Xiao��jun2 |
| 1. Yangzhou University, Yangzhou 225009, Jiangsu, China;2. Northeastern University, Shenyang 110025, Liaoning, China |
|
|
|
|
Abstract The isothermal and cyclic oxidizing kinetics of Co��40Cr alloy and its lanthanum ion��implanted samples were studied at 1 000 �� in air by thermal gravimetric analysis (TGA). Scanning electron microscopy (SEM) was used to examine the Cr2O3 oxide film��s morphology after oxidation. Secondary ion mass spectrum (SIMS) method was used to examine the binding energy change of chromium caused by La��doping and its influence on the formation of Cr2O3 film. Acoustic emission (AE) method was used in situ to monitor the cracking and spalling of oxide films during oxidizing and subsequent air��cooling stages. Laser Raman spectrum was used to examine the stress changes within oxide films. A theoretical model was proposed relating to the film fracture process and was used to analyze the AE spectrum both on time domain and AE��event number domain. It was found that lanthanum implantation remarkably reduced the isothermal oxidizing rate of Co��40Cr and improved the anti��cracking and anti��spalling properties of Cr2O3 oxide film. The reasons for the improvement were mainly that the implanted lanthanum reduced the grain size and internal stress of Cr2O3 oxide, increased the high temperature plasticity of oxide film, and remarkably reduced the number and size of Cr2O3/Co��40Cr interfacial defects.
|
|
Received: 01 January 1900
|
|
|
|
| [1] |
Yu-cheng Lei,,*,Xiao-kai Guo,Hong-xia Chang,Tian-qing Li,,Qiang Zhu,Gang Chen, Long-ren Xiao. Cavitation erosion behavior of CLAM steel weld joint in liquid lead-bismuth eutectic alloy[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 935-942. |
| [2] |
Ying-yi Zhang,Wei Lv,Xue-wei Lv,Chen-guang Bai,Ke-xi Han,Bing Song. Oxidation kinetics of ilmenite concentrate by non-isothermal thermogravimetric analysis[J]. Chinese Journal of Iron and Steel, 2017, 24(7): 678-684. |
| [3] |
Rui Wang,Yan-ping Bao,*,Yi-hong Li,Tai-quan Li,Di Chen. Effect of slag composition on steel cleanliness in interstitial-free steel[J]. Chinese Journal of Iron and Steel, 2017, 24(6): 579-585. |
| [4] |
Hong-huan Mao,Xing Qi,Jing Cao,Li-cong An,Yi-tao Yang*. Effect of Si on high temperature oxidation of 30Cr13 stainless steel[J]. Chinese Journal of Iron and Steel, 2017, 24(5): 561-566. |
| [5] |
Yong-jiang Huang,,,*,Peng Xue,Xiang Cheng,Ya-ming Wang,Fu-yang Cao,**, Zhi-liang Ning, Jian-fei Sun,. Plasticity improvement of a Zr-based bulk metallic glass by micro-arc oxidation[J]. Chinese Journal of Iron and Steel, 2017, 24(4): 416-420. |
| [6] |
Shi-lu Zhao,*,Zhen Zhang,Jun Zhang,Jian-ming Wang,Zheng-gui Zhang,Shuang-hong Wang. High temperature oxidation resistance of CrN/(Ti,Al,Zr,Cr)N bilayer films deposited by multi-arc ion plating[J]. Chinese Journal of Iron and Steel, 2017, 24(3): 343-349. |
|
|
|
|
2008, Vol. 15 