| Silicon Pick��up of Interstitial��Free Steel From MgO��SiC Refractories |
WEI Yao��wu1,LI Nan1,CHEN Xiao��xia1,HU Tie��shan2,
RAO Jiang��ping2,TAO Xiao��lin2 |
| 1. Hubei Province Key Lab of Refarctories and Ceramics, Wuhan University of Science and Technology, Wuhan 430081, Hubei, China;2. No��3 Steelmaking Plant of Wuhan Iron and Steel Group Corporation, Wuhan 430082, Hubei, China |
|
|
|
|
Abstract The silicon pick��up of interstitial��free steel (IF steel) from resin bonded MgO��SiC refractories is studied via a medium frequency induction furnace. Samples of IF steel were heated in MgO��SiC crucibles with mould flux cover at 1 600 �� for 180 min. The silicon contents of IF steel samples taken from the molten steel in every 30 min were examined and the refractories after heating were investigated by electron probe microanalysis (EPMA) with energy dispersive spectrometer (EDS). The silicon content of steel rapidly increased in the first 90 min of heating, and then decreased because of the formation of liquid layer on the refractory. Liquid layer separated the liquid steel from the bulk refractory and stopped the pick��up of silicon. At the same time, desilication via oxygen through the liquid layer and flux started to reduce the silicon content of the liquid steel.
|
|
Received: 01 January 1900
|
|
|
|
| [1] |
Hai-yan Tang*,Yong Wang,Guang-hui Wu,Peng Lan,Jia-quan Zhang. Inclusion evolution in 50CrVA spring steel by optimization of refining slag[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 879-887. |
| [2] |
H. Gonzalez,J.A. Ramos-Banderas,E. Torres-Alonso,G. Solorio-Diaz,C.A. Hern��ndez-Bocanegra,. Multiphase modeling of fluid dynamic in ladle steel operations under non-isothermal conditions[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 888-900. |
| [3] |
Zong-ye Ding,Di Zhang,Qiao-dan Hu,,*,Long Zeng,Jian-guo Li,. Constitutive analysis and optimization on hot working parameters of as-cast high Cr ultra-super-critical rotor steel with columnar grains[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 916-924. |
| [4] |
Hao Li,Yan-chong Yu,,Xiang Ren,Shao-hua Zhang,She-bin Wang,,*. Evolution of Al2O3 inclusions by cerium treatment in low carbon high manganese steel[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 925-934. |
| [5] |
Yu-cheng Lei,,*,Xiao-kai Guo,Hong-xia Chang,Tian-qing Li,,Qiang Zhu,Gang Chen, Long-ren Xiao. Cavitation erosion behavior of CLAM steel weld joint in liquid lead-bismuth eutectic alloy[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 935-942. |
| [6] |
Zhen Cao,Shu-qi Wang*,Ke-zhi Huang,Bo Zhang,Guo-hong Wen,Qiu-yang Zhang,Lan Wang. Effect of artificial tribological layer on sliding wear behavior of H13 steel[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 943-949. |
|
|
|
|
2008, Vol. 15 