| Influence of size of hematite powder on its deoxidation kinetics with H2 at low temperature |
| GUO Pei-min |
|
|
|
|
Abstract The deoxidation kinetics of hematite ore with various particle sizes with hydrogen at low temperature and reduction mechanisms were studied using the thermogravimetric analysis. Under the same temperature, after particle size of powder becomes thinner from 107.5��m to 2��m, the surface area of powder and the contact area between powder and gas increase, which makes the deoxidation process of hematite accelerate about 8 times, and the apparent activation energy of deoxidation reaction drops to 36.9 kJ/mol from 78.3 kJ/mol because of activity of ore powder improved with refining gradually. Under the same reaction rate, the reaction temperature of 6.5��m powder decreases about 80�� than that of 107.5��m powder. Thinner diffusion layer also helps accelerate the reaction with powder refining. The higher the temperature, the greater peak of deoxidation rate is; under the same temperature, the greater the particle size, the smaller the peak of deoxidation rate is; both inner diffuse and interface chemical reaction play an important role in the whole reaction process.
|
|
Received: 24 March 2008
|
|
|
|
| [1] |
Hui Guo,Peng Zhou,*,Ai-min Zhao,,Chao Zhi,Ran Ding,Jia-xing Wang. Effects of Mn and Cr contents on microstructures and mechanical properties of low temperature bainitic steel[J]. Chinese Journal of Iron and Steel, 2017, 24(3): 290-295. |
| [2] |
Yong LI,Fu-chun ZHOU,Zhao-xin ZHOU,Zhi-han TIAN,Chao YANG,Xi-ke TIAN. An Innovative Approach to Separate Iron Oxide Concentrate from High-sulfur and Low-grade Pyrite Cinders[J]. Chinese Journal of Iron and Steel, 2016, 23(8): 756-764. |
| [3] |
Xi- min ZANG,Tian- yu QIU,Wan- ming LI,Xin DENG,Zhou- hua JIANG,,Hua SONG. Electroslag Remelting Withdrawing Technology for Offshore Jack- up Platform Rack Steel Manufacturing Process[J]. Chinese Journal of Iron and Steel, 2016, 23(4): 297-304. |
| [4] |
M. BALAKRISHNAN,V. BALASUBRAMANIAN,M��A. MUTHU MANICKAM. Evaluation of Zero and Sub-zero Temperature Tensile and Impact Properties of Quenched and Tempered Steel Weldments[J]. Chinese Journal of Iron and Steel, 2016, 23(11): 1177-1187. |
| [5] |
K S Abdel Halim. Theoretical Approach to Change Blast Furnace Regime With Natural Gas Injection[J]. Chinese Journal of Iron and Steel, 2013, 20(9): 40-46. |
| [6] |
YANG Da-zheng,QI Dian-wei,XU Peng-fei,ZHANG Da-kui,MA Guang-yu,LI Jing. Sintered Ore Sprayed by Acid and Alkaline Waste Water Resulted From Cold Rolling[J]. Chinese Journal of Iron and Steel, 2013, 20(3): 36-38. |
|
|
|
|
2009, Vol. 16 