| Three-Dimensional Morphology and Growth Behavior of Ferrite Allotriomorphs Formed at Grain Boundary Edges |
WAN Xiang-liang, CHENG Lin, WU Kai-ming |
|
|
|
|
Abstract Three-dimensional morphology of ferrite allotriomorphs nucleated on grain boundary edges in a low carbon steel were revealed by means of serial sectioning in conjunction with computer-aided three-dimensional reconstruction techniques. The typical morphology of ferrite allotriomorphs nucleated on grain boundary edges was of an elongated triangular pyramid. The length, width and thickness of ferrite allotriomorphs were measured on the basis of 3-D reconstructed images. The aspect ratio (length/width) of ferrite allotriomorphs was 4.5 on an average and scattered from 3 to 6. The measured sizes from the 3-D reconstructed images were smaller than those calculated, which was probably attributed to solute drag-like effect of manganese in the alloy.
|
|
Received: 12 October 2009
|
|
Corresponding Authors:
K. M. Wu
|
|
|
|
| [1] |
Ming MA,Hua DING,Zheng-you TANG,Jing-wei ZHAO,Zhou-hua JIANG,Guang-wei FAN. Effects of Temperature and Strain Rate on Flow Behavior and Microstructural Evolution of Super Duplex Stainless Steel under Hot Deformation[J]. Chinese Journal of Iron and Steel, 2016, 23(3): 244-252. |
| [2] |
Min LIU,,Wen-jie ZHENG,Jin-zhong XIANG,Zhi-gang SONG,En-xiang PU,,Han FENG. Grain Growth Behavior of Inconel 625 Superalloy[J]. Chinese Journal of Iron and Steel, 2016, 23(10): 1111-1118. |
| [3] |
LI Qun;WANG Tian-sheng;et al. Warm Deformation Behavior of Steels Containing Carbon of 0.45% to 1.26% With Martensite Starting Structure[J]. Chinese Journal of Iron and Steel, 2010, 17(5): 34-37. |
| [4] |
H��seyin AYDIN. Effect of Intercritical Annealing Parameters on Dual Phase Behavior of Commercial Low-Alloyed Steels[J]. Chinese Journal of Iron and Steel, 2010, 17(4): 0-73. |
| [5] |
XU Feng-yun;WANG Yong-wei. CCT Curves of low carbon Mn-Si steels and development of water cooled bainitic steels[J]. Chinese Journal of Iron and Steel, 2010, 17(3): 46-50. |
| [6] |
M.H. Shaeri. Effects of Austempering and Martempering Processes on Amount of Retained Austenite in Cr-Mo Steels (FMU-226) Used in Mill Liner[J]. Chinese Journal of Iron and Steel, 2010, 17(2): 53-53. |
|
|
|
|
2010, Vol. 17 