Development of Ti��Microalloyed 600 MPa Hot Rolled High Strength Steel |
YI Hai��long, LIU Zhen��yu, WANG Guo��dong, et al |
|
|
Abstract A high strength steel with tensile strength on the order of 710MPa had been development successfully with only addition of titanium alloy element based on a low carbon steel. The results show the hot deformation accelerates ferrite and pearlite transformation and retards bainite transformation under continuous cooling condition. The microstructure of this steel is mainly composed of fine-grained ferrite and carbides distributed along the ferrite grain boundaries. The yield and tensile strengths of steels are about 620��650MPa and 720��740MPa, respectively, and the values of strain hardening exponent (n) and plastic strain ratio (r) are 0.12 and 0.80, respectively, thus providing well-matched strength with toughness. In short, the fine-grained ferrite and TiC nano-precipitates play an effective role in strengthening the steel.
|
Received: 16 November 2009
|
|
|
|
[1] |
Xu Yang,,Bo Liao,Fu-ren Xiao,Wei Yan,Yi-yin Shan,Ke Yang. Ripening behavior of M23C6 carbides in P92 steel during aging at 800��C[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 858-864. |
[2] |
Zhi-gang Song,En-xiang Pu,. Precipitated phases of superaustenitic stainless steel 654SMO[J]. Chinese Journal of Iron and Steel, 2017, 24(7): 743-749. |
[3] |
Reng-chong Xu,,Yan-lin He,,Hu Jiang,,Hua Wang,,Na-qiong Zhu,,Xiao-gang Lu,, Lin Li,. Microstructures and mechanical properties of ferrite-based lightweight steel with different compositions[J]. Chinese Journal of Iron and Steel, 2017, 24(7): 737-742. |
[4] |
Shi-lu Zhao,*,Zhen Zhang,Jun Zhang,Jian-ming Wang,Zheng-gui Zhang,Shuang-hong Wang. High temperature oxidation resistance of CrN/(Ti,Al,Zr,Cr)N bilayer films deposited by multi-arc ion plating[J]. Chinese Journal of Iron and Steel, 2017, 24(3): 343-349. |
[5] |
Zhi-gang Song*,Han Feng,Shao��mei Hu. Development of Chinese duplex stainless steel in recent years[J]. Chinese Journal of Iron and Steel, 2017, 24(2): 121-130. |
[6] |
Hai-feng Xu,,*,Feng Yu,Chang Wang,Wan-li Zhang,Jian Li,Wen-quan Cao. Comparison of microstructure and property of high chromium bearing steel with and without nitrogen addition[J]. Chinese Journal of Iron and Steel, 2017, 24(2): 206-213. |
|
|
|
|