Quantitative Analysis of Non-Crystalline and Crystalline Solids in Blast Furnace Slag |
WANG Hai��feng, ZHANG Chun��xia, QI Yuan��hong |
|
|
Abstract China is short of water seriously. But granulation of blast furnace slag (BFS) with water has many disadvantages, such as high water consumption and difficulty in heat recycling. So developing a new dry granulation technique to treat BFS is very important. The applicability of BFS directly depends on the content of non-crystalline solids in the slag after treatment. So it is of theoretical and practical significance to analyze the content of non-crystalline solids in the slag quantitatively and simply. Metallographical test is mainly adopted to quantify the non-crystalline in BFS now with the shortages such as making sample complexly, determining difficultly and personally. For the diffraction intensity of non-crystalline is proportionate to the content of non-crystalline in BFS, X-ray diffraction method was adopted to quantify the non-crystalline and the crystalline solids in BFS. The quantificational coefficient between the crystalline and the non-crystalline solids of BFS is 0.70 whose main composition is: w��CaO��38.2%��w��SiO2��35.7%��w��Al2O3��16.3%��w��MgO��8.3%. The relatively error of using X-ray diffraction instrument to quantitative analyse non-crystalline content of BFS is less than 1%.
|
Received: 04 January 2010
|
Corresponding Authors:
WANG Hai-Feng
|
|
|
|
[1] |
Qian-qian Ren,,Yu-zhu Zhang,,*,Yue Long,Shao-sheng Chen,Zong-shu Zou,Jie Li, Chen-guang Xu. Crystallization behavior of blast furnace slag modified by adding iron ore tailing[J]. Chinese Journal of Iron and Steel, 2017, 24(6): 601-607. |
[2] |
Xiao-juan ZHEN,Pei-qing LA,Cui-ling LI,Su-lei HU. Effects of Different Substrates on Microstructures and Mechanical Properties of a Bulk Nanocrystalline Structure Pure Iron Prepared by Aluminothermic Reaction Casting[J]. Chinese Journal of Iron and Steel, 2015, 22(4): 324-329. |
[3] |
Chun-bo HUANG,,Tian-cheng LIU,,Xiang-yue WANG,,Cao-wei LU,,De-ren LI,,Zhi-chao LU,. Magnetic Properties of Nanocrystalline Powder Cores Fabricated by Mechanically Crushed Powders[J]. Chinese Journal of Iron and Steel, 2015, 22(1): 67-71. |
[4] |
Chun-bo HUANG,,Tian-cheng LIU,,Xiang-yue WANG,,Cao-wei LU,,De-ren LI,,Zhi-chao LU,. Magnetic Properties of Nanocrystalline Powder Cores Using Mechanically Crushed Powders[J]. Chinese Journal of Iron and Steel, 2014, 21(3): 348-351. |
[5] |
HAO Yun��wei;DENG Bo;ZHONG Cheng;JIANG Yi��ming;LI Jin. Effect of Surface Mechanical Attrition Treatment on Corrosion Behavior of 316 Stainless Steel[J]. Chinese Journal of Iron and Steel, 2009, 16(2): 68-0. |
[6] |
NI Hong��wei;HE Hang;LI Guang��qiang;LIU Jing. Preparation of Nanocrystalline 430L Stainless Steel by HEBM and SPS[J]. Chinese Journal of Iron and Steel, 2008, 15(4): 73-0. |
|
|
|
|