| Fatigue Property of Low Cost and High Strength Wheel Steel for Commercial Vehicle |
| WANG Ning,LI Yi,DU Lin��xiu,WU Di,LIU Xiang��hua |
| The State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110004, Liaoning, China |
|
|
|
|
Abstract The fatigue properties of the newly developed wheel steel used for commercial vehicles were studied using push��pull axial loading fatigue tests with stress ratio R=-1. Q235B steel, which is conventionally applied to commercial vehicle wheels, was also analyzed for comparison. Although the chemical composition and microstructure (ferrite and pearlite) of newly developed wheel steel were similar to those of Q235B, the 107 cycles fatigue limit of the new wheel steel was 260 MPa, which is 24% higher than that of Q235B (210 MPa). The improvement of the fatigue strength of the new wheel steel can be attributed to grain refinement. In order to investigate the effect of the decrease in thickness of the wheel steel on the fatigue property of the wheel, dynamic cornering fatigue tests were conducted on full scale wheels with the model of 8��25��22��5. The results indicated that the newly developed wheel steel had outstanding fatigue life even if the mass loss was 10% in comparison with Q235B.
|
|
Received: 01 January 1900
|
|
|
|
| [1] |
Yu Xu,,En-gang Wang,,*,Zhuang Li,,An-yuan Deng,. Effects of vertical electromagnetic stirring on grain refinement and macrosegregation control of bearing steel billet in continuous casting[J]. Chinese Journal of Iron and Steel, 2017, 24(5): 483-489. |
| [2] |
Chun-yu Zhang,Rui-bin Gou,Min Yu,*,Ya-jing Zhang,Yin-hu Qiao,Shu-ping Fang. Mechanical and fatigue properties of self��piercing riveted joints in high-strength steel and aluminium alloy[J]. Chinese Journal of Iron and Steel, 2017, 24(2): 214-221. |
| [3] |
Zheng CHEN,,Qi��jie ZHAI,Jie��yu ZHANG,Hong��gang ZHONG. Effects of Thermal Gradients and Rotational Flows on Grain Growth in 22 t Steel Ingots[J]. Chinese Journal of Iron and Steel, 2016, 23(9): 973-980. |
| [4] |
Gen LIANG,,Chen SHI,,Ya-jun ZHOU,,Da-heng MAO,. Numerical Simulation and Experimental Study of an Ultrasonic Waveguide for Ultrasonic Casting of 35CrMo Steel[J]. Chinese Journal of Iron and Steel, 2016, 23(8): 772-777. |
| [5] |
Xiang-dong HUO,Lie-jun LI,Zheng-wu PENG,Song-jun CHEN. Effects of TMCP Schedule on Precipitation, Microstructure and Properties of Ti-microalloyed High Strength Steel[J]. Chinese Journal of Iron and Steel, 2016, 23(6): 593-601. |
| [6] |
Jia-tao ZHANG,Yu-guang ZHAO,Juan TAN,Xiao-feng XU. Austenite Grain Refinement by Reverse ������� Transformation in Metastable Austenitic Manganese Steel[J]. Chinese Journal of Iron and Steel, 2015, 22(2): 157-162. |
|
|
|
|
2009, Vol. 16 