| Fatigue Properties of Supersteel for Automobiles |
DU Lin��xiu1,ZHANG Zhong��ping1,2,TIAN Yu��wei3,
LIU Xiang��hua1,WANG Guo��dong1 |
| 1. State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110004, Liaoning, China;2. Hot Rolled Strip Plant, Panzhihua Steel, Panzhihua 617062, Sichuan, China; 3. Technology Center, Benxi Steel Group, Benxi 117000, Liaoning, China |
|
|
|
Abstract gy Center, Benxi Steel Group, Benxi 117000, Liaoning, China)
Abstract�� The fatigue properties of 400 MPa grade supersteel, plain low carbon steel SS400 and microalloyed steel Q340TM were investigated through tensile��compression fatigue experiment with R=-1. The results indicate that the fatigue limit of the 400 MPa supersteel is higher than that of SS400 steel and close to that of the 340TM steel. According to the analysis of fatigue fracture, the fatigue striations of supersteel SS400 is thinner than that of SS400 steel and 340TM steel, and grain refinement can increase the fatigue limit.
|
|
Received: 01 January 1900
|
|
|
|
| [1] |
LI Jun��ZHANG Ling-ling��ZHAO Gui-zhou��CANG Da-qiang. Pilot practice of direct modification of molten blast furnace slag and preparation of mineral wool fiber[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 99-103. |
| [2] |
XU Ren-ze��ZHANG Jian-liang��ZHANG He-shun��LIU Chang-jiang�� FAN Xiao-yue��WANG Zhi-yu. Influence of TiO2 on properties of Jingtang blast furnace slag and thermodynamic analysis[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 104-108. |
| [3] |
JIANG Zhou-hua��ZHANG Xin-fa��LIU Fu-bin��GONG Wei. Harmful impurities control of raw material used in Ni-based superalloy production[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 1-10. |
| [4] |
SONG Guang-yi��YANG Quan��WANG Xiao-chen��ZHANG Xi-bang�� WANG Feng-mei��WANG Qiu-na. Work roll wear law for hot strip temper mill[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 54-59. |
| [5] |
WANG Bing-xing��XIONG Lei��ZHANG Tian��WANG Zhao-dong��WANG Guo-dong. Influence on deformation permeability of plate by controlled rolling process with inter-pass water cooling technology[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 60-65. |
| [6] |
YU Hui��ZHAI Jian-wei��ZHANG Chao-fan��LIU Shuai-shuai��LIU Li-gang. Microstructures and properties of nuclear carbon manganese steels P280GH after accelerated aging[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 66-72. |
|
|
|
|
2006, Vol. 13 