Effect of Ce on Inclusions and Impact Property of 2Cr13 Stainless Steel |
LIU Xiao, YANG Ji��chun, YANG Lin, et al
|
|
|
Abstract The effect of Ce on inclusions and impact toughness of 2Cr13 stainless steel were studied by SEM and electron spectroscopy. Thermodynamic calculation was used to analyze the formation of RE inclusions in 2Cr13 stainless steel. The result shows that Al2O3 and MnS can be entirely replaced by Ce2O2S and CeS. Fracture is changed from cleavage to ductile fracture by adding Ce to the 2Cr13 stainless steel, and the spherical rare earth oxysulfide inclusions-Ce2O2S in the dimple are the main factors. The transverse impact value of 2Cr13 stainless steel has been improved obviously by rare earth. The transverse impact value of RE-2Cr13 is increased 55.46% at the temperature of -40��, comparing with 0RE-2Cr13.
|
Received: 21 October 2009
|
|
|
|
[1] |
Hai-yan Tang*,Yong Wang,Guang-hui Wu,Peng Lan,Jia-quan Zhang. Inclusion evolution in 50CrVA spring steel by optimization of refining slag[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 879-887. |
[2] |
Hao Li,Yan-chong Yu,,Xiang Ren,Shao-hua Zhang,She-bin Wang,,*. Evolution of Al2O3 inclusions by cerium treatment in low carbon high manganese steel[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 925-934. |
[3] |
Jia-long Tian,,Wei Wang,,Wei Yan,,Zhou-hua Jiang,Yi-yin Shan,,Ke Yang. Microstructure characteristics of segregation zone in 17-4PH stainless steel piston rod[J]. Chinese Journal of Iron and Steel, 2017, 24(7): 718-723. |
[4] |
Liang Yang,,Bryan A. Webler,Guo-guang Cheng. Precipitation behavior of titanium nitride on a primary inclusion particle during solidification of bearing steel[J]. Chinese Journal of Iron and Steel, 2017, 24(7): 685-690. |
[5] |
Rui Wang,Yan-ping Bao,*,Yi-hong Li,Tai-quan Li,Di Chen. Effect of slag composition on steel cleanliness in interstitial-free steel[J]. Chinese Journal of Iron and Steel, 2017, 24(6): 579-585. |
[6] |
Ze-an Lv,,Hong-wei Ni,,*,Hua Zhang,,Cheng-song Liu,,**. Evolution of MnS inclusions in Ti-bearing X80 pipeline steel[J]. Chinese Journal of Iron and Steel, 2017, 24(6): 654-660. |
|
|
|
|