Thermodynamic Calculation of Carbide Precipitate in Niobium Microalloyed Steels |
XU Yun��bo,YU Yong��mei,LIU Xiang��hua,WANG Guo��dong |
State Key Lab of Rolling and Automation, Northeastern University, Shenyang 110004, Liaoning, China |
|
|
Abstract On the basis of regular solution sublattice model, thermodynamic equilibrium of austenite/carbide in Fe��Nb��C ternary system was investigated. The equilibrium volume fraction, chemical driving force of carbide precipitates and molar fraction of niobium and carbon in solution at different temperatures were evaluated respectively. The volume fraction of precipitates increases, molar fraction of niobium dissolved in austenite decreases and molar fraction of carbon increases with decreasing the niobium content. The driving force increases with the decrease of temperature, and then comes to be stable at relatively low temperatures. The predicted ratio of carbon in precipitates is in good agreement with the measured one.
|
Received: 01 January 1900
|
|
|
|
[1] |
LI Jun��ZHANG Ling-ling��ZHAO Gui-zhou��CANG Da-qiang. Pilot practice of direct modification of molten blast furnace slag and preparation of mineral wool fiber[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 99-103. |
[2] |
XU Ren-ze��ZHANG Jian-liang��ZHANG He-shun��LIU Chang-jiang�� FAN Xiao-yue��WANG Zhi-yu. Influence of TiO2 on properties of Jingtang blast furnace slag and thermodynamic analysis[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 104-108. |
[3] |
JIANG Zhou-hua��ZHANG Xin-fa��LIU Fu-bin��GONG Wei. Harmful impurities control of raw material used in Ni-based superalloy production[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 1-10. |
[4] |
SONG Guang-yi��YANG Quan��WANG Xiao-chen��ZHANG Xi-bang�� WANG Feng-mei��WANG Qiu-na. Work roll wear law for hot strip temper mill[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 54-59. |
[5] |
WANG Bing-xing��XIONG Lei��ZHANG Tian��WANG Zhao-dong��WANG Guo-dong. Influence on deformation permeability of plate by controlled rolling process with inter-pass water cooling technology[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 60-65. |
[6] |
YU Hui��ZHAI Jian-wei��ZHANG Chao-fan��LIU Shuai-shuai��LIU Li-gang. Microstructures and properties of nuclear carbon manganese steels P280GH after accelerated aging[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 66-72. |
|
|
|
|