Isothermal Grain Growth of Austenite in Hypoeutectoid and Hypereutectoid Plain Carbon Steels |
Joydeep Maity, Dipak Kumar Mondal |
|
|
Abstract Grain growth kinetics of austenite in a hypoeutectoid steel (containing 0.35 wt% carbon) at 920��C and in a hypereutectoid steel (containing 1 wt% carbon) at 980��C has been investigated with holding time ranging from 1 h to 6 h. The hypoeutectoid steel exhibited normal grain growth without solute drag hindrance with a time exponent (0.51) close to the theoretical value (0.5). However, grain growth of austenite in hypereutectoid steel was extremely slow up to 3 h of holding characterized by a low value of time exponent (0.06). Thereafter, a breakaway occurred and the grain growth in hypereutectoid steel from 3 h to 6 h of holding progressed normally with a time exponent (0.55) close to the theoretical value (0.5).
|
Received: 07 September 2009
|
|
|
|
[1] |
Jian-guo Chen,Yong-chang Liu,Chen-xi Liu,Bi-yu Yan,Hui-jun Li. Effects of tantalum on austenitic transformation kinetics of RAFM steel[J]. Chinese Journal of Iron and Steel, 2017, 24(7): 705-710. |
[2] |
Geng-wei YANG,,,Xin-jun SUN,Qi-long YONG,Zhao-dong LI,Xiao-xian LI,. Austenite Grain Refinement and Isothermal Growth Behavior in a Low Carbon Vanadium Microalloyed Steel[J]. Chinese Journal of Iron and Steel, 2014, 21(8): 757-764. |
[3] |
Han MA,Shu-lun LIAO,Shi-fang WANG. Effect of Ti on Austenite Grain Growth Behavior in High Carbon Steels[J]. Chinese Journal of Iron and Steel, 2014, 21(7): 702-709. |
[4] |
Lin CHENG,Kai-ming WU,Xiang-liang WAN,Guo-hong ZHANG. Growth Kinetics of Proeutectoid Ferrite in an Fe-0.09C-1.5Mn-0.2Si Steel[J]. Chinese Journal of Iron and Steel, 2014, 21(10): 964-968. |
[5] |
YAO Sheng��jie,DU Lin��xiu,LI Guang��long,JIAO Xing,WANG Guo��dong. Microstructure Evolving Behaviors of Undercooled Ultrafine Austenite Grains During Deformation[J]. Chinese Journal of Iron and Steel, 2011, 18(6): 43-48. |
[6] |
DUAN Lin-na. Austenite Grain Growth Behavior of X80 Pipeline Steel in Heating Process[J]. Chinese Journal of Iron and Steel, 2010, 17(3): 62-66. |
|
|
|
|