Influence of Bath Composition on Magnetic Properties of Electrodeposited Co��Pt��W Thin Films |
GE Hong��liang,WEI Guo��ying,WU Qiong,ZHOU Qiao��ying,WANG Xin��yan |
College of Material Science and Engineering, China Jiliang University, Hangzhou 310018, Zhejiang, China |
|
|
Abstract Effect of bath composition ([Co2+]/[Pt��] and [WO2-4], [cit-]) and pH on the magnetic properties of electrodeposited Co��Pt��W thin films has been investigated. Electrodeposited Co��Pt��W thin films exhibited strong perpendicular magnetic anisotropy when the ratio of [Co2+] to [Pt��] was 10; cathode current efficiency and perpendicular magnetic anisotropy showed little variations when [WO2-4] was lower than 0��1 mol/L, but perpendicular magnetic anisotropy had strengthened when [WO2-4] was over 0��1 mol/L, which could be explained by the fact that the hydrogen evolution could produce pores as magnetic domain pinnings; citrate as complexing reagent can promote the polarization of [Co2+] and [Pt��]. As a result, the equilibrium electrode potentials of cobalt and platinum moved to negative direction, which led to the co��deposition of Co, Pt, and W. It was also found out that the as��deposited Co��Pt��W hard magnetic thin films were very homogeneous, smooth, and had the maximum coercivity for the bath pH 8��5 and the concentration of citrate 0��26 mol/L.
|
Received: 01 January 1900
|
|
|
|
[1] |
Hong-ru Ren,Jin-tao Gao,Zhe Wang,Chong Li,Fu-qiang Wang,Zhan-cheng Guo. Evolution of microstructure, mechanical and magnetic properties of electrodeposited 50%Ni-Fe alloy foil after thermal treatment[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 844-851. |
[2] |
Wan-li Zhao,Ding-hao Miao,Yong Zhang*,Zhan-bing He. Big-data analysis of phase-formation rules in high-entropy alloys[J]. Chinese Journal of Iron and Steel, 2017, 24(4): 358-365. |
[3] |
Yi LI,,Yuan��fei LI,Ben XU,Qiu��lin LI,Guo��gang SHU,Wei LIU,. Magnetic Properties of Thermally Aged Fe��Cu Alloys with Pre��deformation[J]. Chinese Journal of Iron and Steel, 2016, 23(9): 981-987. |
[4] |
Zhao-yang CHENG,Jing LIU,Wen-si CHEN,Jia-chen ZHU,Xi-feng LIN,Zhi-dong XIANG. Effect of 0��5 mass% Cu Addition on Ductility and Magnetic Properties of Fe-6��5Si Alloy[J]. Chinese Journal of Iron and Steel, 2016, 23(7): 717-721. |
[5] |
J. SALINAS B.,A. SALINAS R.. Evaluation of Microstructure and Magnetic Properties in Non-oriented Electrical Steel Strained by Tension[J]. Chinese Journal of Iron and Steel, 2016, 23(2): 166-170. |
[6] |
Hai-jun WANG,Bing FU,,Li XIANG,Zhe RONG,Sheng-tao QIU. Effect of Nitrogen Content on Primary Recrystallization Behavior and Magnetic Property of Hi-B Steel[J]. Chinese Journal of Iron and Steel, 2016, 23(10): 1080-1085. |
|
|
|
|