Fe��Mo��B Enhanced Sintering of P/M 316L Stainless Steel |
YANG Xia,GUO Shi��ju |
Institute of Powder Metallurgy, University of Science and Technology Beijing, Beijing 100083, China |
|
|
Abstract Liquid��phase enhanced sintering of powder metallurgy (P/M) 316L stainless steel by addition of sintering aids was studied. 2%-8% of pre��alloyed Fe��Mo��B powder with two different particle sizes was added as sintering aids, and the specimens were sintered in vacuum at 1 200-1 350 ��. The results show that the fine Fe��Mo��B powder (5-10 ��m) has stronger activated effect. The sintered density increases with the increase in sintering aid content or sintering temperature. Warm compaction has a better effect on the control of dimensional precision of compacts. The prealloyed Fe��Mo��B powder deviated from Mo2FeB2 component can also be sintering aid of P/M 316L stainless steel.
|
Received: 01 January 1900
|
|
|
|
|
|
|