| Experimental Study and Kinetic Calculation on Migration of ��/�� Interface Boundary During High Temperature Aging in 2205 Duplex Stainless Steel |
| LIU Xiong, DING Xing-ping, HE Yan-lin, et al |
|
|
|
|
Abstract Aging treatments at the temperature range of 1000-1200 �� for different time intervals (10, 30, 60min) in a solution-treated 2205 duplex stainless steel(DSS) are carried out respectively. The migration of ��/�� interface boundary after different ageing treatments is measured by optical metallography and calculated by DICTRA software. The agreement of the calculation and experimental results is satisfied. The migration of ��/�� interface boundary with increased keeping time depends on the chemical potential of chromium in each phase. At the aging temperature of 1100��, the back diffusion effect of chromium results in the opposite direction migration of ��/�� interface, therefore, the ferrite volume fraction gets lower at first and then gets higher after 1800s diffusion
|
|