Activity Model of Fe��Si��B Ternary Metallic Melts |
ZHAO Ding��guo,GUO Pei��min,ZHAO Pei |
|
|
Abstract According to the ion and molecule coexistence theory, the activity model of Fe��Si��B ternary system was established, and the influence of ratio xSi/xFe, boron content and temperature, etc�� on the activity of the melt compound was investigated. The results show that the FeB activity is high in the liquid iron, when xSi/xFe is 0��5; the activity of boron increases with increasing the boron content for different contents of xFe and xSi, and the activity of boron at the ratio xFe=0��4 is about one order of magnitude higher than that for the xFe=0��8; The activities of the melt compound were also affected by temperature, but the influencing extent was little. The equal activity diagrams of silicon and boron were drawn for the first time according to the model results.
|
Received: 09 June 2010
Published: 15 June 2011
|
|
|
|
[1] |
Hua��qiang HAO,,Yu��zhu ZHANG,,Su��ju HAO,Chao��fa ZHANG,Wu��feng JIANG,Peng��hui CUI. Preparation and Metallurgical Analysis of High Activity Burnt Lime for Steelmaking[J]. Chinese Journal of Iron and Steel, 2016, 23(9): 884-890. |
[2] |
ANG,,Yan-ping BAO,. e and Control of Nitrogen for X70 Pipeline Steel[J]. Chinese Journal of Iron and Steel, 2016, 23(7): 647-654. |
[3] |
Ya-yu LI,Zhen-nan LIU,Dong-ping TAO. An Estimation of Component Activity of Vanadium-bearing Liquid Iron and Transition Temperature of Vanadium Oxidization Using MIVM[J]. Chinese Journal of Iron and Steel, 2015, 22(7): 557-565. |
[4] |
Lei GAN,,Hai-feng WANG,Xiu-ping LI,Yuan-hong QI,Chun-xia ZHANG. Strength Activity Index of Air Quenched Basic Oxygen Furnace Steel Slag[J]. Chinese Journal of Iron and Steel, 2015, 22(3): 219-225. |
[5] |
Sheng-fu ZHANG, Liang-ying WEN, Kun WANG, Chong ZOU, Jian XU. Effects of Additives on Sulfur Transformation, Crystallite Structure and Properties of Coke during Coking of High-sulfur Coal[J]. Chinese Journal of Iron and Steel, 2015, 22(10): 897-904. |
[6] |
Guo-hua ZHANG,, Kuo-chih CHOU,. Deoxidation of Molten Steel by Aluminum[J]. Chinese Journal of Iron and Steel, 2015, 22(10): 905-908. |
|
|
|
|