Warm Deformation Microstructure of a Plain Carbon Steel |
B Eghbali,M Shaban |
Department of Materials Science Engineering, Sahand University of Technology |
|
|
Abstract Grain refinement in a plain carbon steel under intercritical warm deformation was studied by torsion testing. Based on the experimental results, the warm flow behaviour and microstructural evolution of ferrite were researched with particular emphasis on the effect of the strain rate in controlling the grain refinement mechanism of ferrite. The deformed microstructures were investigated at various strain rates using optical microscopy and electron back-scattered diffraction (EBSD). The EBSD observations indicate that an increase in the strain rate leads to the development of new fine ferrite grains with high angle boundaries. Furthermore, it shows that the annihilation of dislocations occurs more readily at lower strain rate. The elongated ferrite grains continuously dynamically recrystallize to form the equiaxed fine ferrite grains. Thereby, the aspect ratio of elongated grains decreases with increasing the strain rate. Furthermore, the peak stress and steady state stress of ferrite both increase with increasing strain rate. Based on the study, the effect of strain rate on the development of fine ferrite grains during continuous dynamic recrystallization of ferrite was analyzed in detail.
|
Received: 14 April 2010
Published: 22 July 2011
|
|
|
|
[1] |
LI Jun��ZHANG Ling-ling��ZHAO Gui-zhou��CANG Da-qiang. Pilot practice of direct modification of molten blast furnace slag and preparation of mineral wool fiber[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 99-103. |
[2] |
XU Ren-ze��ZHANG Jian-liang��ZHANG He-shun��LIU Chang-jiang�� FAN Xiao-yue��WANG Zhi-yu. Influence of TiO2 on properties of Jingtang blast furnace slag and thermodynamic analysis[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 104-108. |
[3] |
JIANG Zhou-hua��ZHANG Xin-fa��LIU Fu-bin��GONG Wei. Harmful impurities control of raw material used in Ni-based superalloy production[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 1-10. |
[4] |
SONG Guang-yi��YANG Quan��WANG Xiao-chen��ZHANG Xi-bang�� WANG Feng-mei��WANG Qiu-na. Work roll wear law for hot strip temper mill[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 54-59. |
[5] |
WANG Bing-xing��XIONG Lei��ZHANG Tian��WANG Zhao-dong��WANG Guo-dong. Influence on deformation permeability of plate by controlled rolling process with inter-pass water cooling technology[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 60-65. |
[6] |
YU Hui��ZHAI Jian-wei��ZHANG Chao-fan��LIU Shuai-shuai��LIU Li-gang. Microstructures and properties of nuclear carbon manganese steels P280GH after accelerated aging[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 66-72. |
|
|
|
|