Investigation on Non-Metallic Inclusions in LCAK Steel Produced by BOF-LF-FTSC Production Route |
YANG Wen1,CAO Jing1,WANG Xin-hua1,XU Zhi-rong2,YANG Jie2 |
1. School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083,China 2. No.1 Steelmaking Plant, Tangshan Iron and Steel Co Ltd, Tangshan 063000, Hebei, China |
|
|
Abstract The behavior of non-metallic inclusions in LCAK (low carbon aluminum killed) steel produced by BOF (basic oxygen furnace)-LF (ladle furnace) refining-FTSC (flexible thin slab continuous caster) production route was investigated. The results showed that, LF refining for LCAK steel could decrease the wT[O] significantly, and the inclusions were modified by Ca treatment, which prevented nozzle clogging efficiently. However, owing to the unstable casting condition in the earlier stage of casting, a severe reoxidation occurred, accompanied with mold slag entrapment. The transformation of non-metallic inclusions during the steelmaking process was Al2O3��MgO-Al2O3 type inclusion��MgO-Al2O3-CaO type inclusion with a CaS ring, and the mechanism of the transformation was proposed and discussed via thermodynamic and kinetic analysis. Besides, to avoid CaS precipitation, the product of w2[Al]��w3[S] in steel should be less than 2.0��10-10 at 1873 K, which remands higher desulfurization ratio during LF refining.
|
Received: 01 June 2010
Published: 26 September 2011
|
|
|
|
[1] |
WANG Yang,CUI Heng,WANG Zheng ,YANG He. Effect of RH circulation time and holding time on cleanliness of IF steel[J]. Chinese Journal of Iron and Steel, 2017, 29(8): 649-653. |
[2] |
CHEN Xiao,BAO Yan-ping,LI Ren-chun,CHEN Jun-li,LI Tai-quan,WANG Rui. Analysis of cleanliness for IF steel slabs at start of continuous casting[J]. Chinese Journal of Iron and Steel, 2017, 29(4): 281-286. |
[3] |
ZHAI Jun,,LI Jian-min,,,LANG Wei-yun,LIU Liu. Effect of LF refining slag basicity on composition of inclusions in 304 stainless steel[J]. Chinese Journal of Iron and Steel, 2017, 29(2): 117-122. |
[4] |
JIANG Teng-fei��ZHU Liang��LIU Feng-gang��ZHAO Xiao-dong��LUO Yan-zhao. Recycling of desulfurization slag in pretreatment of hot metal[J]. Chinese Journal of Iron and Steel, 2017, 52(2): 24-27. |
[5] |
ZHANG Wei-gang����HAN Shun��LI Yong��HUANG Shun-zhe MENG Qing����ZHOU Yun. Behavior of fatigue fracture of 300M steel for large passenger aircraft[J]. Chinese Journal of Iron and Steel, 2017, 52(10): 83-88. |
[6] |
ZHANG Chun-jie. Analysis of the influence of DC06 steel cleanliness unsteady casting[J]. Chinese Journal of Iron and Steel, 2017, 42(04): 21-25. |
|
|
|
|