Effect of Mg Addition on Inhibiting Austenite Grain Growth in Heat Affected Zones of Ti-Bearing Low Carbon Steels |
ZHU Kai1,2,YANG Jian2,WANG Rui-zhi2,YANG Zhen-guo1 |
1. Department of Materials Science, Fudan University, Shanghai 200433, China 2. Metallurgical Process Department, Research and Development Center, Baoshan Iron and Steel Co Ltd, Shanghai 201900, China |
|
|
Abstract To study the effect of Mg addition on inhibiting weld heat affected zones (HAZ) austenite grain growth of Ti-bearing low carbon steels, two steels with and without Mg treated were prepared using a laboratory vacuum. The welding testing was simulated by Gleeble 3500 thermomechanical simulator. The performance of HAZ was investigated that the toughness was improved from 33 to 185 J by adding 0.005% Mg (in mass percent) to the steel, and the fracture mechanism changed from cleavage fracture to toughness fracture. Through in-situ observation by a confocal scanning laser microscope, a significant result was found that the austenite grain of the steel with Mg treated was still keeping fine-grained structure after holding at 1400 �� and lasting for 300 s. This inhibition of austenite grain growth was mainly attributed to the formation of pinning particles after the addition of Mg. The obtained results propose a potential method for improving HAZ toughness of structure steels.
|
Received: 15 July 2010
Published: 26 September 2011
|
|
|
|
[1] |
WANG Li,,LI Guang- qiang,,,LIU Yu,,ZHANG Zhao,,LI Ya- wei��XU Xiao- feng. Interaction between ultra- low carbon liquid steel and MgO- C refractories containing different carbon contents[J]. Chinese Journal of Iron and Steel, 2017, 29(8): 616-625. |
[2] |
BI Chuan-guang��LONG Hong-ming��CHUN Tie-jun��ZHANG Yan-hua. Effect of[ w(MgO)]on properties of oxidized pellets[J]. Chinese Journal of Iron and Steel, 2017, 52(7): 22-26. |
[3] |
LI Jie��XIN Zi-cheng��YANG Ai-min��ZHANG Yu-zhu��LIU Lian-ji��SONG Ya-xian. Effect of basicity on quality of magnesium fluxed pellets[J]. Chinese Journal of Iron and Steel, 2017, 52(7): 35-41. |
[4] |
GAO Sheng-ya��JIANG Min��HOU Ze-wang��WANG Xin-hua. Effect of calciumtreatment on non-metallic inclusions in high carbon aluminum killed steel[J]. Chinese Journal of Iron and Steel, 2017, 52(4): 25-30. |
[5] |
LUO Yan-zhao��JI Chen-xi��DENG Xiao-xuan��PAN Hong-wei��ZENG Zhi��CUI Yang. Optimization of mold flux to improve surface quality of ultra-low carbon IF steel[J]. Chinese Journal of Iron and Steel, 2017, 52(4): 38-43. |
[6] |
XIE Ying��xiu,JIN Xin��yan,,WANG Li,. Development and application of hot��dip galvanized zinc��aluminum��magnesium coating[J]. Chinese Journal of Iron and Steel, 2017, 29(3): 167-174. |
|
|
|
|