Effect of TaC Particles Dissolution on Grain Coarsening in Reduced Activation Steels |
XIA Zhi-xin1,ZHANG Chi1,HUANG Qun-ying2,LIU Shao-jun2,LI Zhao-dong1,YANG Zhi-gang1 |
1. Key Laboratory of Advanced Materials of Ministry of Education, Department of Materials Science and Engineering, Tsinghua University, Beijing 100084, China 2. Institute of Plasma Physics, ChineseAcademy of Sciences, Hefei 230031, Anhui, China |
|
|
Abstract The effect of TaC on grains and packets coarsening in the reduced activation ferritic/martensitic (RAFM) steels was investigated. It was found that the combined effect of the austenitizing temperature and heating rate resulted in the heterogeneous austenite grain growth. When the austenitizing temperature was raised above 1423 K, the TaC particles disappeared, and the homogenous grains abruptly increased. The thermodynamic model for dissolution of TaC particles during austenitizing was applied to interpret the results.
|
Received: 27 July 2010
Published: 26 September 2011
|
Corresponding Authors:
ZhiXin Xia
E-mail: xzx08@mails.tsinghua.edu.cn
|
|
|
|
|
|
|