Development of Continuous Casting Technology of Electrical Steel and New Products |
WANG Li-tao1,DENG Chen-hong2,DONG Mei1,SHI Li-fa1,ZHANG Jian-ping1 |
1. Technology Center, Maanshan Iron and Steel Co Ltd, Ma��anshan 243000, Anhui, China 2. Central Iron and Steel Research Institute, Beijing 100081, China |
|
|
Abstract The development of continuous casting technology of electrical steel was analyzed. The technologies and products characteristics of conventional continuous casting, thin slab continuous casting and rolling, middle thin slab continuous casting and rolling and twin-roll thin strip were compared. Conventional continuous casting technology was widely adopted in producing electrical steel; thin slab continuous casting and rolling and middle thin slab continuous casting and rolling technology industrialized electrical steel; and study of twin-roll thin strip casting technology was focused on fundamental experiments.
|
Received: 13 September 2011
Published: 23 February 2012
|
Corresponding Authors:
Chen-hong DENG
E-mail: dengch3313@126.com
|
|
|
|
[1] |
J. SALINAS B.,A. SALINAS R.. Evaluation of Microstructure and Magnetic Properties in Non-oriented Electrical Steel Strained by Tension[J]. Chinese Journal of Iron and Steel, 2016, 23(2): 166-170. |
[2] |
Ai-hua CHEN,Hai-rong GUO,Hua-long LI,Toshihiko EMI. Formation of Edge Crack in 1��4%Si Non-oriented Electrical Steel during Hot Rolling[J]. Chinese Journal of Iron and Steel, 2014, 21(2): 269-274. |
[3] |
SHAO Yuan-yuan,YANG Ping,FU Yong-jun,,MAO Wei-min. Texture Evolution of Columnar Grains in Electrical Steel During Hot Rolling[J]. Chinese Journal of Iron and Steel, 2013, 20(10): 99-106. |
[4] |
WANG Jian;LI Jun;WANG Xin-feng;et al. Effect of Heating Rate on Microstructure Evolution and Magnetic Properties of Cold Rolled Non-Oriented Electrical Steel[J]. Chinese Journal of Iron and Steel, 2010, 17(11): 54-61. |
[5] |
XIANG Li;YUE Er��bin;FAN Ding��dong;QIU Sheng��tao;ZHAO Pei. Calculation of AlN and MnS Precipitation in Non��Oriented Electrical Steel Produced by CSP Process[J]. Chinese Journal of Iron and Steel, 2008, 15(5): 88-0. |
|
|
|
|