Influence of Aluminum Content on Mechanical Properties and Cold Workability of Fe-33Ni-15Co Alloy |
M Safavi1,S M Abbasi2,R Mahdavi3 |
[1. Department of Materials Science and Engineering, Semnan University, Semnan 54896, Iran 2. Advanced Materials Research Laboratory AMRL, Department of Mechanical Engineering, K��N�� Toosi University of Technology, Tehran 45987, Iran 3. Department of Materials Science, Azad University, Teran 16597, Iran] |
|
|
Abstract The influence of 0��01% to 0��25% of Aluminum content (in mass percent) on the mechanical properties and cold workability of low thermal expansion Fe-33Ni-15Co sheets in the annealed and hot rolled condition was investigated. Addition of Al up to 0��15% resulted in the increase of ductility and toughness and improvement of workability. Besides, achievement of fine grain structure and increase in the amount of annealing twins caused ductility to improve. Addition of Al higher than 0��15% led to the increase in oxidation reaction during melting process and to refine under argon atmosphere. This caused the volume fraction of Al containing inclusions to increase and consequently the ductility and toughness to decrease.
|
Received: 23 November 2010
Published: 23 February 2012
|
|
|
|
[1] |
LI Jun��ZHANG Ling-ling��ZHAO Gui-zhou��CANG Da-qiang. Pilot practice of direct modification of molten blast furnace slag and preparation of mineral wool fiber[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 99-103. |
[2] |
XU Ren-ze��ZHANG Jian-liang��ZHANG He-shun��LIU Chang-jiang�� FAN Xiao-yue��WANG Zhi-yu. Influence of TiO2 on properties of Jingtang blast furnace slag and thermodynamic analysis[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 104-108. |
[3] |
JIANG Zhou-hua��ZHANG Xin-fa��LIU Fu-bin��GONG Wei. Harmful impurities control of raw material used in Ni-based superalloy production[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 1-10. |
[4] |
SONG Guang-yi��YANG Quan��WANG Xiao-chen��ZHANG Xi-bang�� WANG Feng-mei��WANG Qiu-na. Work roll wear law for hot strip temper mill[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 54-59. |
[5] |
WANG Bing-xing��XIONG Lei��ZHANG Tian��WANG Zhao-dong��WANG Guo-dong. Influence on deformation permeability of plate by controlled rolling process with inter-pass water cooling technology[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 60-65. |
[6] |
YU Hui��ZHAI Jian-wei��ZHANG Chao-fan��LIU Shuai-shuai��LIU Li-gang. Microstructures and properties of nuclear carbon manganese steels P280GH after accelerated aging[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 66-72. |
|
|
|
|