| Effect of Basicity and Alumina-Silica Ratio on Formation of Silico-Ferrite of Calcium and Aluminum |
| ZHANG Fang1,2,AN Sheng-li1,LUO Guo-ping1,2,WANG Yi-ci1,2 |
1. School of Materials and Metallurgy, Inner Mongolia University of Science and Technology, Baotou 014010,Inner Mongolia, China
2. School of Metallurgical and Ecological Engineering University of Science and Technology Beijing, Beijing 100083, China |
|
|
|
|
Abstract Abstract�� Baivumebo iron ore is special magnetite containing fluorine, kalium and sodium elements, and the main raw material for ironmaking of Baotou Iron and Steel (Group) Co. The effects of basicity and ratio of Al2O3 to SiO2 (A/S) on the formation of silico-ferrite of calcium and aluminium (SFCA) in Baivumebo low silica sinters were studied by means of mini-sintering, XPF-500 optical mineralogical microscope and CSS-88000 electronic universal testing machine. The results show that it is beneficial to the formation of complex calcium ferrite to enhance the basicity of Baivumebo low silica sinters. The acicular SFCA-I was increased with the enhancing basicity and reached the peak at basicity 2��8, then the columnar or platy SFCA formed and the bonding strength decreased. Alumina is beneficial to the formation of acicular complex calcium ferrite in Baivumebo low silica sinters. But the residual unfused Al2O3 reagent came into being when A/S was 0��35, while complex calcium ferrite still remained to be acicular. There is a common rule about mineralogy components affected by basicity and ratio of A/S, that is, SFCA is increasing accompanied with hematite and porosity reduced, but the content of glass phase is stable.
|
|
Received: 30 January 2011
Published: 02 May 2012
|
|
|
|
| [1] |
Qian-qian Ren,,Yu-zhu Zhang,,*,Yue Long,Shao-sheng Chen,Zong-shu Zou,Jie Li, Chen-guang Xu. Crystallization behavior of blast furnace slag modified by adding iron ore tailing[J]. Chinese Journal of Iron and Steel, 2017, 24(6): 601-607. |
| [2] |
Xin-yu LI,Bu-xin SU,Lei-ge XIA,Jian-liang ZHANG,Hong-wei GUO. Effect of Nickel on Formation Mechanisms of Silico-ferrite of Calcium and Aluminum (SFCA)[J]. Chinese Journal of Iron and Steel, 2015, 22(6): 478-486. |
| [3] |
Yousef MOHASSAB, Hong-yong SOHN. Effect of Water Vapor on O2? Content in Ironmaking Slag[J]. Chinese Journal of Iron and Steel, 2015, 22(10): 909-915. |
| [4] |
Azza Ahmed,Hossam Halfa,Mohamed K. El-Fawakhry,Hoda El-Faramawy,Mamdouh Eissa. Parameters Affecting Energy Consumption for Producing High Carbon Ferromanganese in a Closed Submerged Arc Furnace[J]. Chinese Journal of Iron and Steel, 2014, 21(7): 666-672. |
| [5] |
REN Zhong-shan,,HU Xiao-jun,,CHOU Kuo-chih,. Calculation and Analysis of Sulfide Capacities for CaO-Al2O3-SiO2-MgO-TiO2 Slags[J]. Chinese Journal of Iron and Steel, 2013, 20(9): 21-25. |
| [6] |
AN Xiu-wei,WANG Jing-song,LAN Rong-zong,HAN Yi-hua,XUE Qing-guo. Softening and Melting Behavior of Mixed Burden for Oxygen Blast Furnace[J]. Chinese Journal of Iron and Steel, 2013, 20(5): 11-16. |
|
|
|
|
2012, Vol. 19 