| Failure Mechanism and Material Requirements for Coal Lance in Blast Furnac |
| XIONG Wei,JIA Juan,CHEN Jia-chao,SHANG He-ming |
| Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education,Wuhan University of Science and Technology, Wuhan 430081, Hubei, China |
|
|
|
|
Abstract Abstract�� Pulverized coal injection (PCI) is a key technology in modern ironmaking by blast furnace (BF) and the life of injection lance has a great influence on PCI operation and on normal running of blast furnace. It is found that the main reasons for the failure of the lances are their outer surface oxidation and the inner surface erosion through monitoring some lances used in BF. The outer surface oxidation of the lances made of lCr18Ni9Ti is inevitable under high hot blast temperature condition through thermodynamics analysis. A mathematical model for calculating the temperature of common monocular coal lance had been developed according to the principles of mass and energy balance. Increasing temperature and flow velocity of the hot blast would cause a rise in the lance temperature. The influence of hot blast temperature is more obvious. The lance temperature would decline when compressed air flux increases. Conveying technology of dense phase pulverized coal is beneficial to extending lance��s life because decreasing solid-gas ratio would intensify erosion and burning loss. The anti-oxidation temperature of lance materials needs to be over 1000 �� for BF intensified smelting. In order to increase the resistance to oxidation of the coal lance��s outer surface, oxidation-resistant steel or Al coating stainless steel is the appropriate material for BF use. Employing the metal surface treatment technology to enhance the hardness of the coal lance��s internal surface could prolong the service life of coal lance.
|
|
Received: 21 February 2011
Published: 02 May 2012
|
|
Corresponding Authors:
Wei Xiong
E-mail: xiongwei@wust.edu.cn
|
|
|
|
| [1] |
LI Jun��ZHANG Ling-ling��ZHAO Gui-zhou��CANG Da-qiang. Pilot practice of direct modification of molten blast furnace slag and preparation of mineral wool fiber[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 99-103. |
| [2] |
XU Ren-ze��ZHANG Jian-liang��ZHANG He-shun��LIU Chang-jiang�� FAN Xiao-yue��WANG Zhi-yu. Influence of TiO2 on properties of Jingtang blast furnace slag and thermodynamic analysis[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 104-108. |
| [3] |
WANG Hai-yang��ZHANG Jian-liang��WANG Guang-wei��LI Tao��JIANG Xi��. Feasibility research of injection of BF dust into melter gasifier of COREX[J]. Chinese Journal of Iron and Steel, 2017, 52(8): 29-34. |
| [4] |
LONG Yue,,DU Pei-pei,,ZHANG Liang-jin,,LI Zhi-hui,, ,ZHANG Yu-zhu,. Impact of various factors on property and fiber-forming effect of centrifugal blast furnace slag fibers[J]. Chinese Journal of Iron and Steel, 2017, 29(7): 530-535. |
| [5] |
YAN Chao-jie,LI Fu-min,QIE Ya-na,LIU Song,L�� Qing. Effect of hydrogen content of bosh gas on iron ore dropping process[J]. Chinese Journal of Iron and Steel, 2017, 29(6): 441-446. |
| [6] |
HAN Wei-gang��LI Xiu-ping��LIU Jian-hua��ZHANG Chun-xia��ZHOU Ji-cheng��SHI Xin-yue. Temperature drop of hot metal during BF tapping in Shougang Jingtang[J]. Chinese Journal of Iron and Steel, 2017, 52(6): 13-17. |
|
|
|
|
2012, Vol. 19 