| Experimental Study on Deep Desulfurizer in LF Process |
| WU Long1,PEI Fen2,CHEN Yu3,LI Shi-qi1 |
1. Metallurgical and Ecological Engineering School, University of Science and Technology Beijing, Beijing 100083,China
2. Beijing Shenwu Environment and Energy Technology Company Group, Beijing 102200, China
3. Xinxing Pipes Xinjiang Resources Development Limited Company, Urumqi 830000, Xinjiang, China |
|
|
|
|
Abstract Abstract�� CaO-Al2O3-SiO2-CaF2-MgO was selected as the slag system for desulfurization in LF process. The reaction between steel and slag during desulfurization has been simulated by using Factsage software to study the influence of component on the sulfur distribution ratio. In order to research the influence of CaO content, aluminum powder content and its granularity on desulfurization, laboratory experiments have been carried out in a 200 kg inductive furnace. Results showed that the optimal composition of deep desulfurizer is wCaO=64% and aluminium powder 10% with a granularity of 30 ��m. Industrial trials showed that the main composition range of final slag in LF process is wCaO=53��0%-57��0%, wAl2O3=23��4%-25��1%, wSiO2=8��1%-10��0%, and wCaF2=3��2%-4��7%. The sulfur mass percent in steel is lower than 0��0008% with a desulfurization rate above 89%. According to the result of industrial production, this desulfurizer could meet the production requirement for ultra-low sulfur steel, of which sulfur mass percent is under 0��0015%.
|
|
Received: 02 March 2011
Published: 02 May 2012
|
|
Corresponding Authors:
Wu Long
E-mail: jieke8857@126.com
|
|
|
|
| [1] |
ZHOU Li,LIANG Jian,WANG Xiang- hong,ZHANG Ping,SHI Xiao- fang. Effect of refining slag with different basicities and low alumina content on inclusion composition of spring steel[J]. Chinese Journal of Iron and Steel, 2017, 29(8): 626-636. |
| [2] |
WANG Jian-zhong. Discussion about the production of GCr15 bearing steel by 150 t BOF-LF��RH��-CC process[J]. Chinese Journal of Iron and Steel, 2017, 35(4): 58-62. |
| [3] |
ZHAI Jun,,LI Jian-min,,,LANG Wei-yun,LIU Liu. Effect of LF refining slag basicity on composition of inclusions in 304 stainless steel[J]. Chinese Journal of Iron and Steel, 2017, 29(2): 117-122. |
| [4] |
CHEN Peng- ju,,ZHU Cheng- yi,,,ZHANG Zhi- cheng,LI Guang- qiang,,PAN Ming- xu. Thermodynamic evaluation of desulfurization ability of GCr15 bearing steels during LF refining process[J]. Chinese Journal of Iron and Steel, 2016, 28(5): 30-35. |
| [5] |
GE Jin-peng�� LI Jing�� SHI Cheng-bin�� WANG Peng. Effect of high-basicity refining slag on cleanliness of bearing steel GCr15[J]. Chinese Journal of Iron and Steel, 2016, 51(11): 30-35. |
| [6] |
XU Ji-fang,��ZHANG Jie-yu,��SU Li-juan,��SHENG Min-qi,��WENG Wen-ping. Melting temperature and viscosity-temperature characteristics ofAl2O3-CaO base pre-molten re.ning slag[J]. Chinese Journal of Iron and Steel, 2015, 27(8): 17-23. |
|
|
|
|
2012, Vol. 19 