Optimization Study of Calcium Leaching From Steelmaking Slag |
XU An-jun1,2,ZHANG Hui-ning1,2,YANG Yi1,2,CUI Jian3,HE Dong-feng1,2,TIAN Nai-yuan1,2 |
1. State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing, Beijing 100083,China 2. School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing,Beijing 100083, China 3. Ningbo Iron and Steel Co Ltd, Ningbo 315000, Zhejiang, China |
|
|
Abstract Abstract�� In order to study calcium leaching behavior for the steelmaking slag, factors that influence the leaching yield have been optimized. The results show that granularity of the slag, liquid to solid ratio (in short for L/S), temperature and reaction time have a significant effect on the leaching yield. The optimal conditions for leaching are determined as follows: 1) the granularity at 75 ��m, L/S at 100, temperature at 60 ��; 2) the granularity at 75 ��m, L/S at 50, temperature at 40 ��. Finally, the optimal leaching yield under these conditions is about 15%.
|
Received: 02 August 2011
Published: 02 May 2012
|
Corresponding Authors:
XU An-Jun
E-mail: maple_prince@sohu.com
|
|
|
|
[1] |
LIU Hong-qiang��FU Jian-xun��LIU Si-yu��XIE Xin-yue��YANG Xiao-ying. Calculation methods and application of carbon dioxide emission during steel-making process[J]. Chinese Journal of Iron and Steel, 2016, 51(4): 74-82. |
[2] |
ZHANG Hui-ning��LAI Chao-bin��LU Yong-ming��XU An-jun��HE Dong-feng��TIAN Nai-yuan. Kinetic model of calcium leaching for steelmaking slag based on Gamma particle size distribution[J]. Chinese Journal of Iron and Steel, 2015, 50(5): 81-87. |
[3] |
CHEN Yong-xing,WANG Guang-wei,ZHANG Jian-liang,SU Bu-xin,ZUO Hai-bin. Theoretical Analysis of Injecting Coke Oven Gas With Oxygen Enriched Into Blast Furnace[J]. Chinese Journal of Iron and Steel, 2012, 47(2): 12-16. |
[4] |
ZHAO Yan-qiang1,2,LI Xiao-chun3,LI Gui-ju1,2. Current Situation of CO2 Emission and Point Sources Distribution in China��s Iron and Steel Industry[J]. Chinese Journal of Iron and Steel, 2012, 24(05): 1-4. |
[5] |
LU Ming1��ZHU Rong1��BI Xiu-rong1��WEI Ning1��WANG Can-rong2��KE Jian-xiang2. Fundamental Research on Dephosphorization of BOF by COMI Steelmaking Process[J]. Chinese Journal of Iron and Steel, 2011, 46(8): 31-35. |
[6] |
QIAN Qiang. Experimental Study of Neutralization of Vanadium��Bearing Converter Slag With Waste Titanium Dioxide Spent Acid[J]. Chinese Journal of Iron and Steel, 2009, 44(2): 80-0. |
|
|
|
|