Precipitation of AlN and MnS in Low Carbon Aluminium-Killed Steel |
CHEN Yin-li,WANG Yan,ZHAO Ai-min |
Engineering Research Institute, University of Science and Technology Beijing, Beijing 100083, China |
|
|
Abstract Abstract�� The precipitation kinetics of AlN and MnS in low carbon aluminium-killed steel was calculated. Transmission electron microscopy (TEM), energy disperse spectroscopy (EDS) and phase analyses have been used to investigate the morphology, compositions and particle size distribution of AlN and MnS precipitates in three positions of the coil. The particles of AlN and MnS precipitates in the ferrite region after coiling and distributes along and adjacent to the ferrite grain boundaries. The shapes of AlN are plate-like, the precipitates size is about 10 to 60 nm; the shapes of MnS are spherical, the precipitates size is about 200 to 600 nm. The precipitation behavior of AlN is sensitive to the isothermal temperature and holding time, the precipitation quantity and particle size distribution of AlN in different positions of coil are unequal.
|
Received: 07 January 2011
Published: 02 May 2012
|
Corresponding Authors:
Yinli CHEN
E-mail: yinli_chen@ustb.edu.cn
|
|
|
|
[1] |
LI Jun��ZHANG Ling-ling��ZHAO Gui-zhou��CANG Da-qiang. Pilot practice of direct modification of molten blast furnace slag and preparation of mineral wool fiber[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 99-103. |
[2] |
XU Ren-ze��ZHANG Jian-liang��ZHANG He-shun��LIU Chang-jiang�� FAN Xiao-yue��WANG Zhi-yu. Influence of TiO2 on properties of Jingtang blast furnace slag and thermodynamic analysis[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 104-108. |
[3] |
JIANG Zhou-hua��ZHANG Xin-fa��LIU Fu-bin��GONG Wei. Harmful impurities control of raw material used in Ni-based superalloy production[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 1-10. |
[4] |
SONG Guang-yi��YANG Quan��WANG Xiao-chen��ZHANG Xi-bang�� WANG Feng-mei��WANG Qiu-na. Work roll wear law for hot strip temper mill[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 54-59. |
[5] |
WANG Bing-xing��XIONG Lei��ZHANG Tian��WANG Zhao-dong��WANG Guo-dong. Influence on deformation permeability of plate by controlled rolling process with inter-pass water cooling technology[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 60-65. |
[6] |
YU Hui��ZHAI Jian-wei��ZHANG Chao-fan��LIU Shuai-shuai��LIU Li-gang. Microstructures and properties of nuclear carbon manganese steels P280GH after accelerated aging[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 66-72. |
|
|
|
|