Influence of Normal Load, Sliding Speed and Ambient Temperature on Wear Resistance of ZG42CrMo |
ZHANG Jian1,2,PENG Yan1,2,LIU Hong-min1,2,LIU Yun-fei1,2 |
1. National Engieering Research Center for Equipment and Technology of Cold Rolling Strip, Yanshan University, Qinhuangdao 066004, Hebei, China 2. State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004, Hebei, China |
|
|
Abstract Abstract�� To investigate the wear resistance of ZG42CrMo in industrial application, the wear behaviors under different normal loads, sliding speeds and ambient temperatures were simulated by an MMU-5G abrasion tester to acquire the friction coefficients and wear rates, with the morphology of worn surface observed by scanning electron microscopy (SEM) and chemical composition of worn surface and debris analyzed by X-ray energy dispersive spectroscopy (EDS). Combine with the theory of tribology, finally the regular of environmental factors�� influence on material wear behaviors is determined. The results show that the increase of load decreases wear resistance significantly, when the pressure reaches a certain extent, severe spalling occurs on the worn surface; the changes of speed result in the changes of size of abrasive debris, and then effect the wear behaviors, in the increasing process of speed, the wear rate increases firstly and then decreases; the rise of temperature causes changes in wear mechanism, bring forth oxidation film on the worn surface, which leads to significant improvement of the wear resistance of materials under high temperature compared to that under low temperature.
|
Received: 16 December 2010
Published: 02 May 2012
|
|
|
|
[1] |
ZOU Jin����FU Qing-feng��LU De-ping��ZHOU Zhe��LIU Cheng-cheng��LU Lei. Surface modification of H13 steel by pulse-plasma detonation treatment[J]. Chinese Journal of Iron and Steel, 2017, 52(2): 71-77. |
[2] |
XIA Li- ming��YANG Xi. Abrasive wear property of Fe- Cr- C hardfacing layer reinforced by adding Nb[J]. Chinese Journal of Iron and Steel, 2015, 27(6): 75-79. |
[3] |
XIA Li- ming��YANG Xi. Abrasive wear property of Fe- Cr- C hardfacing layer reinforced by adding Nb[J]. Chinese Journal of Iron and Steel, 2015, 27(12): 75-79. |
[4] |
YUAN Ya-sha��WANG Wen-yan����XU Kai-hui��YUAN Sha��LI Jun-ling. Influence of differential heat treatment on wear resistance of Cr5 steel[J]. Chinese Journal of Iron and Steel, 2015, 50(10): 71-76. |
[5] |
ZHENG Yang,,LIU Zhong-yi,LI Wei,. Abrasion Characteristic Research of Thin Slab Continue Casting and Rolling Low Alloy Wear-Resistant Steel[J]. Chinese Journal of Iron and Steel, 2014, 49(3): 63-67. |
[6] |
HOU Jian-qiang1,FU Han-guang1,JIANG Ye-hua2,ZHOU Rong2,CEN Qi-hong2. Microstructure and Property of Boron-Bearing High Speed Steel Roll[J]. Chinese Journal of Iron and Steel, 2012, 24(08): 38-43. |
|
|
|
|