Effect of Tube Spinning With Subsequent Heat-Treatment on Performance and Microstructure Evolution of T250 Maraging Steel |
HU Zheng-fei1,WANG Chun-xu2 |
1. School of Material Science and Engineering, Tongji University, Shanghai 200092, China 2. China Iron and Steel Institute Group, Beijing 100081, China |
|
|
Abstract The effects of spinning deformation and subsequent heat treatments on the mechanical properties and microstructure of 18Ni Co-free Maraging steel (T250) tube were evaluated comparatively with the perform. An obvious radial shrinkage is detected in spun tubes after heat treatment and the magnitude of the shrinkage induced by solution treatment is almost the same as that by aging. Plastic deformation during spinning elongated the grains severely in the direction of metal flow. The solution treatment resulted in a drastically refined grain and recrystallised microstructure, removing the effect of plastic deformation, relieving the tangential residual stress and strain and improving hardness. Subsequent aging obtained a tempered microstructure, enhancing hardness values strikingly for precipitation strengthening. XRD (X-ray diffraction) analysis indicated that the reversed austenite formed in a plate-like along the grain boundaries and the volume fraction of austenite in spun tube was more than double that in the preform. These results imply that the residual stress and stain induced by spinning process and reversed austenite forming during aging might have the similar contribution to the radical shrinkage.
|
Received: 21 April 2011
Published: 29 May 2012
|
Fund:The National Natural Science Foundation of China |
|
|
|
[1] |
YIN Cun-hong��LIANG Yi-long. Friction induced wear and martensite deformation behavior of 20CrNi2Mo steel[J]. Chinese Journal of Iron and Steel, 2017, 52(8): 81-86. |
[2] |
LEI Dong��REN Yong��CHENG Xiao-ru��LAN Kun��QIU Jun��HUANG Da-jun. Effect of heat treatment on microstructure and mechanical properties of 316L/Q235 stainless steel composite panel[J]. Chinese Journal of Iron and Steel, 2017, 52(5): 66-71. |
[3] |
LIU Ning,,LIU Zheng-dong,,HE Xi-kou,YANG Zhi-qiang. Structure inheritance removing of SA508Gr.4N steel for nuclear reactor pressure vessels[J]. Chinese Journal of Iron and Steel, 2017, 29(5): 402-410. |
[4] |
WANG Chun-fang��LI Yong��LI Nan��LU Yan�� LI Ji-kang. Effect of heat treatment process on critical transformation and CCT curve of AISI4340 steel[J]. Chinese Journal of Iron and Steel, 2017, 52(3): 70-75. |
[5] |
YANG Cai-fu��CHEN Xue-hui��WANG Rui-zhen. Quality assessment and suggestion of standard revision for high strength rebars in China[J]. Chinese Journal of Iron and Steel, 2017, 52(10): 94-103. |
[6] |
LI Ju-bao, ,LI Yan,ZHANG You-yu,YANG Guang-yu. Effect of heat treatment in dual-phase region on microstructure and property of 430 ferritic stainless steel hot rolled sheet[J]. Chinese Journal of Iron and Steel, 2017, 29(1): 62-66. |
|
|
|
|