| Measuring and Modeling of Density for Selected CaO-MgO-Al2O3-SiO2 Slag With Low Silica |
| XU Ji-fang1,ZHANG Jie-yu1,JIE Chang1,TANG Lei1,CHOU Kuo-chih1,2 |
1. Shanghai Key Laboratory of Modern Metallurgy and Material Processing, Shanghai University, Shanghai 200072, China
2. Metallurgical and Ecological Engineering School, University of Science and Technology Beijing, Beijing 100083, China |
|
|
|
|
Abstract The densities of the selected quaternary CaO-MgO-Al2O3-SiO2 slag with low silica were measured by the Archimedean method in a wide temperature range from 1773 to 1873 K. Nine different slag compositions were chosen based on three different levels of CaO content and three different levels of SiO2 content. wMgO was equal to 7.0%. wCaO were varied from 40.04% to 50.64%, for wSiO2=10.25%-20.70%. The effects of temperature, SiO2 content and optical basicity were studied. It is shown that density decreases approximately linearly with an increase in temperature. Under the same CaO content, the density decreases with increasing of SiO2 content, and increases with optical basicity increasing. Based on the experimental data as the boundary of the homogenous phase region predicated by FACTSAGE software, the mass triangle model is used to calculate the density of selected limited homogenous phase region. The results showed that the mass triangle model works well.
|
|
Received: 01 June 2011
Published: 25 July 2012
|
|
Corresponding Authors:
Jie-Yu ZHANG
E-mail: zhangjieyushu@gmail.com
|
|
|
|
| [1] |
LI Jun��ZHANG Ling-ling��ZHAO Gui-zhou��CANG Da-qiang. Pilot practice of direct modification of molten blast furnace slag and preparation of mineral wool fiber[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 99-103. |
| [2] |
ZHAO Lu-peng��WU Keng��ZHU Li����CHEN Xiao-min��QIN Xuan-ke. Prediction model of sinter properties based on BP neural network[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 11-15. |
| [3] |
WANG Bin,YE Dong- dong,CHEN Jian- jun,SUN Quan,AN Qi. Experimental and numerical analysis of compression fracture for strip steel oxidation film[J]. Chinese Journal of Iron and Steel, 2017, 29(9): 762-767. |
| [4] |
LI Xue-tao����JIANG She-ming��ZHANG Qi-fu ��TENG Hua-xiang��ZHAO Hai-feng��HUANG Ming-dong. Kinetics model of non-isothermal austenite phase transformation for hot stamping boron steel[J]. Chinese Journal of Iron and Steel, 2017, 52(8): 92-96. |
| [5] |
DENG Xiao-xuan����JI Chen-xi����AN Ze-qiu��ZHU Guo-sen��SUO Jin-liang��HUANG Fu-xiang. Effect of mold width on level characteristics in continuous casting mold of slab[J]. Chinese Journal of Iron and Steel, 2017, 52(8): 48-54. |
| [6] |
LIU Zi- long,WANG Zhi- meng,XING Peng- da,CAO Wen- quan,PENG Yan,WANG Yu- hui. Static recrystallization behavior of GCr15 bearing steel[J]. Chinese Journal of Iron and Steel, 2017, 29(8): 671-677. |
|
|
|
|
2012, Vol. 19 