Microstructure Evolution in 9Cr Martensitic Steel During Long-Term Creep at 650 �� |
HU Zheng-fei1,WANG Qi-jiang2,ZHANG Bin1 |
1. School of Material Science and Engineering, Tongji University, Shanghai 200092, China 2. Institute of Baosteel, Shanghai 201900, China |
|
|
Abstract Standardarized creep and rupture strength tests were conducted for commercial T91 martensitic heat-resistant steel at 650 �� and corresponding microstructure was characterized by BSED, TEM and EDS. The martensitic microstructure degenerated seriously during creep exposure, including martensitic substructure recovering, carbides coarsening, dissolving and precipitating. EDS analysis shows that the M23C6 carbides in different morphologies have dissimilar compositions. The rod/sheet like M23C6 particles within the matrix contain more additions, which might precipitate in situ while fine MX particles were re-solving. The high content of silicon in these rod/sheet like M23C6 carbides is probably related to self diffusion coefficient increasing for the exposed condition at 650 �� close to Curie temperature Tc. For those reasons, martensite substructure becomes unstable, and microstructure evolution is accelerated and leads to creep strength deteriorating severely.
|
Received: 14 February 2011
Published: 25 July 2012
|
|
|
|
[1] |
XU Tian- han,FENG Yao- rong,WANG Dang- hui. Influence of hydrogen on mixed- mode ��/�� fracture toughness of casing- drilling steels[J]. Chinese Journal of Iron and Steel, 2017, 29(9): 749-755. |
[2] |
HUANG Rui,WANG Huan- rong,LIU Jun- liang. Influence of coiling temperature on nano- precipitated particles of advanced nano- precipitate strengthened high strength steel[J]. Chinese Journal of Iron and Steel, 2017, 29(8): 684-689. |
[3] |
YANG Ting,SU Hang,LUO Xiao-bing,CHAI Feng,ZHANG Zheng-yan. Cross section microstructure and homogeneity of mechanical properties of as quenched high strength ship steel[J]. Chinese Journal of Iron and Steel, 2017, 29(7): 583-589. |
[4] |
LUO Yi-wa����GUO Han-jie����SUN Xiao-lin����. Precipitation behaviors of carbides in M42 high speed steel during ESR and forging[J]. Chinese Journal of Iron and Steel, 2017, 52(7): 68-75. |
[5] |
WANG Dong-chen,LI Xiao-yuan,WEI Li-jin,SHI Jie,WANG Qi,XU Le. Effect of tempering temperature on fracture toughness of high carbon steel[J]. Chinese Journal of Iron and Steel, 2017, 29(6): 494-499. |
[6] |
LEI Dong��REN Yong��CHENG Xiao-ru��LAN Kun��QIU Jun��HUANG Da-jun. Effect of heat treatment on microstructure and mechanical properties of 316L/Q235 stainless steel composite panel[J]. Chinese Journal of Iron and Steel, 2017, 52(5): 66-71. |
|
|
|
|