| Effect of Hf on Stress Rupture Properties of DD6 Single Crystal Superalloy After Long Term Aging |
| SHI Zhen-xue,LI Jia-rong,LIU Shi-zhong |
| National Key Laboratory of Science and Technology on Advanced High Temperature Structural Materials,Beijing Institute of Aeronautical Materials, Beijing 100095, China |
|
|
|
|
Abstract The specimens of the second generation single crystal superalloy DD6 with different Hf contents were prepared in the directionally solidified furnace with a high temperature gradient. The long term aging of the specimens after full heat treatment was performed at 1040 �� for 800 h. The effect of Hf on the microstructure and stress rupture properties under 980 ��/250 MPa of the alloy after long term aging was investigated. The results show that the �á� coarsening and rafting and no topologically close packed phase (TCP) are observed in the microstructures of DD6 alloy with different Hf contents after aged at 1040 �� for 800 h. It indicates that DD6 alloy with different Hf contents all possesses good microstructure stability. With increasing Hf content the rupture life after long term aging turns shorter and the elongation represents the increasing first and decreasing afterwards. The fracture mechanism of the alloy with different Hf contents at 980 ��/250 MPa all shows dimple model. The influence of the microstructures on the stress rupture properties of the alloy is also discussed.
|
|
Received: 08 March 2011
Published: 25 July 2012
|
|
|
|
| [1] |
Zhen-xue Shi,Shi-zhong Liu,Xiao-dai Yue,Li-jie Hu,Wan-peng Yang,Xiao-guang Wang,Jia-rong Li. Effect of cellular recrystallization on tensile properties of a nickel-based single crystal superalloy containing Re and Ru[J]. Chinese Journal of Iron and Steel, 2017, 24(10): 1059-1064. |
| [2] |
Zhen-xue SHI,Shi-zhong LIU,Jian YU,Jia-rong LI. Tensile Behavior of the Second Generation Single Crystal Superalloy DD6[J]. Chinese Journal of Iron and Steel, 2015, 22(8): 738-742. |
| [3] |
SHI Zhen-xue,LIU Shi-zhong,WANG Xiao-guang,LI Jia-rong. Corrosion behavior of the second generation single crystal superalloy DD6 in hot gas[J]. Chinese Journal of Iron and Steel, 2015, 27(5): 61-64. |
| [4] |
SHI Zhen-xue,LI Jia-rong,LIU Shi-zhong,WANG Xiao-guang,YUE Xiao-dai. Effects of Ru on Solidification Characteristic and Microstructures of Ni-Based Single Crystal Superalloy[J]. Chinese Journal of Iron and Steel, 2013, 20(3): 74-78. |
| [5] |
SHI Zhen-xue,HAN Mei,LIU Shi-zhong,LI Jia-rong. Influence of Cast Dimension on Rotary Bending High Cycle Fatigue Properties of Single Crystal Superalloy[J]. Chinese Journal of Iron and Steel, 2013, 20(12): 98-102. |
| [6] |
SHI Zhen-xue,LI Jia-rong,LIU Shi-zhong,ZHAO Jin-qian. Effects of Dendritic Orientation on Stress Rupture Properties of DD6 Single Crystal Superalloy[J]. Chinese Journal of Iron and Steel, 2011, 18(10): 66-71. |
|
|
|
|
2012, Vol. 19 