Simultaneous Recrystallization and Oxidation Behavior of Mn-Containing IF Steel |
ZHANG Zuo-tai,ZHANG Ying-yi |
Department of Energy and Resources Engineering, College of Engineering, Peking University, Beijing 100871, China |
|
|
Abstract The recrystallization and oxidation of a Mn-containing interstitial free (IF) steel were investigated simultaneously using confocal scanning laser microscope (CSLM) under controlled atmosphere of Ar 95% and H2 5% (in volume percent) at different temperatures. It was found that the grain boundary played a significant role in controlling recrystallization and oxidation in overall oxidation kinetics of the steel. The surface morphology was composed of two networks along the original and new grain boundaries respectively, which did not coexist. The grain boundary moved in different directions with different velocities during annealing process. The recrystallization processes were studied by CSLM motion video through observing the moving grain boundary to estimate the time for 50% recrystallization, and the activation energy for recrystallization was therefore calculated. The oxidation mechanism was discussed through comparison of the fluxes among mass transfer of water vapor, dissociation of water vapor and outward diffusion alloying elements. The results indicated that the oxidation was controlled by the mass transfer from the bulk gas to the surface, or dissociation rate, or outward diffusion of manganese, which depended on the temperature to form a grain boundary ridge or groove.
|
Received: 21 April 2011
Published: 28 August 2012
|
Corresponding Authors:
ZHANG Zuo-Tai
E-mail: zuotaizhang@coe.pku.edu.cn
|
|
|
|
[1] |
FAN Ming- qiang,,MAO Lei,,ZHANG Yun- fei,TIAN Zhi- qiang,SUN Zhong- hua,QIN Sen. Effects of temperature rise on deformation behavior and microstructure of H13 steel during high temperature compression process[J]. Chinese Journal of Iron and Steel, 2017, 29(9): 756-761. |
[2] |
WANG Bin,YE Dong- dong,CHEN Jian- jun,SUN Quan,AN Qi. Experimental and numerical analysis of compression fracture for strip steel oxidation film[J]. Chinese Journal of Iron and Steel, 2017, 29(9): 762-767. |
[3] |
GUO Pei-min��ZHAO Pei��WANG Lei��KONG Ling-bing. Oxidizing kinetics of reducing gas during iron oxide reduction process[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 22-26. |
[4] |
JIANG Guang-rui����CHEN Ling-feng��WANG Hai-quan����LIU Jin-sheng��LIU Li-bin��5. Influence of over-aging dew point on surface color difference of dual phase steel[J]. Chinese Journal of Iron and Steel, 2017, 52(8): 87-91. |
[5] |
ZHANG Shi-wei������YANG Ming������LIANG Yi-long������JIANG Yun����LONG Shao-lei����. Constitutive equations and dynamic recrystallization behaviors of 20CrNi2Mo steel at stage of high temperature deformation[J]. Chinese Journal of Iron and Steel, 2017, 52(8): 97-105. |
[6] |
LIU Zi- long,WANG Zhi- meng,XING Peng- da,CAO Wen- quan,PENG Yan,WANG Yu- hui. Static recrystallization behavior of GCr15 bearing steel[J]. Chinese Journal of Iron and Steel, 2017, 29(8): 671-677. |
|
|
|
|