Reduction Behavior of Sinter Based on Top Gas Recycling-Oxygen Blast Furnace |
LAN Rong-zong1,2,WANG Jing-song1,HAN Yi-hua1,SHE Xue-feng1,WANG Lin-tao1,XUE Qing-guo1 |
1. State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing, Beijing 100083, China 2. China Railway Materials Xiamen Steel Co Ltd, Xiamen 361008, Fujian, China |
|
|
Abstract In order to explore the behavior laws of sinter reduction in TGR-OBF (top gas recycling-oxygen blast furnace), reduction experiments of sinter have been conducted by thermal balance mass loss method with different atmospheres, temperatures and volume flows. The changes of RI (reduction degree of Fe2O3), RI�� (reduction rate of Fe2O3) and r (reduction degree of FeO) have been examined. The results show that the reduction of sinter was significantly improved under TGR-OBF atmosphere, and the RI and r were measured up to 98.2% and 97.8% at 900 �� respectively. With increasing of the reduction temperature, the reduction of sinter speeded up greatly, and the reduction time-duration shortened from 117 min at 900 �� to 63 min at 1100 ��. Moreover, the reduction of sinter enhanced with increasing of the reductive gas flow. When the flow increased from 10 to 15 L/min, the initial reduction rate of sinter increased from 2.47%/min to 3.73%/min. While increasing H2 and CO contents in the reductive atmosphere, the reduction of sinter was promoted. Besides, H2 influenced more evidently than CO to the reduction of sinter, especially in the later stage of the reduction process, for instance, the reduction of wustite will be improved enormously when increasing the H2 content in the reductive atmosphere.
|
Received: 01 September 2011
Published: 26 September 2012
|
Fund:National Key Technology R&D Program in the 12th Five year Plan of China |
Corresponding Authors:
Rong-Zong LAN
E-mail: lanrongzong@163.com
|
|
|
|
[1] |
CHANG Jin,ZHANG Xin- jian,LIU Qing- cai,REN Shan,WANG Xiao- qing,ZHOU Jian. Effect of sintering raw materials with municipal sludge on sintering process and sinter quality[J]. Chinese Journal of Iron and Steel, 2017, 29(9): 711-716. |
[2] |
GUO Yu- feng,,GUO Xing- min. Effect of MgO on low temperature reduction process of hematite fines sinter[J]. Chinese Journal of Iron and Steel, 2017, 29(9): 697-703. |
[3] |
ZHAO Lu-peng��WU Keng��ZHU Li����CHEN Xiao-min��QIN Xuan-ke. Prediction model of sinter properties based on BP neural network[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 11-15. |
[4] |
GUO Pei-min��ZHAO Pei��WANG Lei��KONG Ling-bing. Oxidizing kinetics of reducing gas during iron oxide reduction process[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 22-26. |
[5] |
MIN Yi,,FENG Yu- tao,QIN Chong- da,,LI Wen,SHI Pei- yang,,WEI Heng. Effect of municipal solid waste incineration fly ash addition on property of iron ore sinter[J]. Chinese Journal of Iron and Steel, 2017, 29(8): 610-615. |
[6] |
XU Cong-min,ZHANG Xuan,LUO Li-hui,YANG Dong-ping. Corrosion behavior of X100 pipeline steel in near neutral pH soil solution with action of SRB[J]. Chinese Journal of Iron and Steel, 2017, 29(7): 562-569. |
|
|
|
|