| Structure and Corrosion Resistance of a Composite ��-Amino Propyl Triethoxy Silane and ��-Glycidoxy Propyl Trimethoxy Silane Conversion Coating on Galvanized Steel |
| WANG Lei1,2,LIU Chang-sheng1,YU Hai-yun1,AN Cheng-qiang2 |
1. Key Laboratory for Anisotropy and Texture of Materials of Ministry of Education, Northeastern University,Shenyang 110004, Liaoning, China
2. School of Environmental and Chemical Engineering, Shenyang LigongUniversity, Shenyang 110159, Liaoning, China |
|
|
|
|
Abstract In an aqueous solution of the mixtures of ��-amino propyl triethoxy silane and ��-glycidoxy propyl trimethoxy silane, a composite silane conversion coating was developed on galvanized steel. FESEM (field emission scanning electron microscope), XPS (X-ray photoelectron spectroscopy), ATR-FTIR (attenuated total reflection Flourier transform infrared spectroscopy) and SST (salt spray test) were used to characterize the obtained composite silane conversion coating and also the coating formation process was studied. The result showed that the surface of the composite silane conversion coating was complete, consecutive and compact. The coating could endure a neutral salt spray test for 72 h without corrosion. The result of salt spray test indicated that the composite silane conversion coating can provide a better corrosion inhibition than the coating which was composed of the single silane. Based on observation and analysis, it was proposed that the formation process of the silane coating on zinc should consist of three steps: the hydrolysis of the silane molecules, silane chemical adsorption and silane crosslinking condensation. The crosslinking reactions took place between ��-amino propyl triethoxy and ��-glycidoxy propyl trimethoxy silane during the forming process of the coating, and a high crosslinked density interpenetrating structure network was obtained, so the composite silane conversion coating could keep the corrosive substances from the zinc more effectively.
|
|
Received: 15 June 2011
Published: 28 November 2012
|
| Fund:National Hi-Tech Research and Development Program |
|
Corresponding Authors:
Lei Wang
E-mail: mailwl@163.com
|
|
|
|
| [1] |
WANG Xin-dong��LI Jian-xin��LIN Zhang-guo�� XIONG Zi-liu. Product development and technology innovation of automotive sheet in Hesteel Group[J]. Chinese Journal of Iron and Steel, 2017, 52(8): 70-74. |
| [2] |
MIN Yi,,FENG Yu- tao,QIN Chong- da,,LI Wen,SHI Pei- yang,,WEI Heng. Effect of municipal solid waste incineration fly ash addition on property of iron ore sinter[J]. Chinese Journal of Iron and Steel, 2017, 29(8): 610-615. |
| [3] |
YIN Rui-yu. A discussion on ��smart�� steel plant��view from physical system side[J]. Chinese Journal of Iron and Steel, 2017, 52(6): 1-12. |
| [4] |
TIAN Ya-qiang,WANG An-dong,SONG Jin-ying,ZHENG Xiao-ping,ZHAO Ding-guo,CHEN Lian-sheng. Formation reason and control measures of surface quality defects of cold rolled steel sheet for galvanization[J]. Chinese Journal of Iron and Steel, 2017, 29(4): 312-316. |
| [5] |
WANG Yao-zu��ZHANG Jian-liang��LIU Zheng-jian��ZHANG Ya-peng��LIU Dong-hui��DU Cheng-bo. Effects of[w(TiO2)]on mineral structure and softening-melting property of sinter[J]. Chinese Journal of Iron and Steel, 2017, 52(3): 20-28. |
| [6] |
FAN Yi����WANG Qing-feng��YANG Ying��ZHAO Ya-juan. Disscussion about high temperature oxidation behavior of low alloy steel casting slab[J]. Chinese Journal of Iron and Steel, 2017, 35(2): 16-20. |
|
|
|
|
2012, Vol. 19 