| Effect of Nb Solute and NbC Precipitates on Dynamic or Static Recrystallization in Nb Steels |
| XIAO Fu-ren1,CAO Ya-bin1,QIAO Gui-ying2,ZHANG Xiao-bing3,LIAO Bo1 |
1. Key Laboratory of Metastable Materials Science and Technology, College of Materials Science and Engineering,Yanshan University, Qinhuangdao 066004, Hebei, China
2. School of Environmental and Chemical Engineering,Yanshan University, Qinhuangdao 066004, Hebei, China
3. Jiangsu Shagang Group Co Ltd, Zhangjiagang 215625, Jiangsu, China |
|
|
|
|
Abstract Nb is often considered to be a powerful alloying element for controlling the recrystallization process in microalloyed high strength steels. However, Nb can be presented either as solute in solution, where it is thought to exhibit a strong solute drag effect, or as NbC precipitates, which are thought to be effective at pinning grain boundaries. Therefore, it is very important to quantitatively measure Nb in solution or in NbC precipitates. A quantitative analysis method of Nb in solution and in precipitates was proposed. The test procedure involved chemical dissolution, filtration and inductively coupled plasma atomic emission spectroscopic (ICP-AES) analysis. The amount of Nb in solution in Nb-microallyed steels under different treatment conditions was evaluated. The results show that the niobium and carbon contents in steels have a great effect on niobium dissolution kinetics. The solute Nb is more effective to retard dynamic recrystallization, while the NbC precipitates are more effective to inhibit static recrystallization. The results may help to comprehend effect of Nb in steels, and provide some guides in the design of new high strength Nb-bearing steels.
|
|
Received: 27 June 2011
Published: 28 November 2012
|
| Fund:Key Technologies R & D Program of Hebei Province |
|
Corresponding Authors:
Xiao Fu-Ren
E-mail: frxiao@ysu.edu.cn
|
|
|
|
| [1] |
FAN Ming- qiang,,MAO Lei,,ZHANG Yun- fei,TIAN Zhi- qiang,SUN Zhong- hua,QIN Sen. Effects of temperature rise on deformation behavior and microstructure of H13 steel during high temperature compression process[J]. Chinese Journal of Iron and Steel, 2017, 29(9): 756-761. |
| [2] |
ZHANG Shi-wei������YANG Ming������LIANG Yi-long������JIANG Yun����LONG Shao-lei����. Constitutive equations and dynamic recrystallization behaviors of 20CrNi2Mo steel at stage of high temperature deformation[J]. Chinese Journal of Iron and Steel, 2017, 52(8): 97-105. |
| [3] |
LIU Zi- long,WANG Zhi- meng,XING Peng- da,CAO Wen- quan,PENG Yan,WANG Yu- hui. Static recrystallization behavior of GCr15 bearing steel[J]. Chinese Journal of Iron and Steel, 2017, 29(8): 671-677. |
| [4] |
HUANG Rui,WANG Huan- rong,LIU Jun- liang. Influence of coiling temperature on nano- precipitated particles of advanced nano- precipitate strengthened high strength steel[J]. Chinese Journal of Iron and Steel, 2017, 29(8): 684-689. |
| [5] |
HUANG Xiang-bin,BAO Si-qian,ZHAO Gang,XU Yang,SONG Na-na,LIU Bing-bing. Primary recrystallization kinetics and texture evolution during annealing of low temperature grain-oriented silicon steel[J]. Chinese Journal of Iron and Steel, 2017, 29(7): 577-582. |
| [6] |
GONG Qian-jiang��������LIANG Yi-long������ ��YANG Ming��������JIANG Yun��������XU Xiang������. Phenomenological constitutive model and dynamic recrystallization behavior of 20CrMnTiH steel[J]. Chinese Journal of Iron and Steel, 2017, 52(6): 67-75. |
|
|
|
|
2012, Vol. 19 