| Effects of Rolling and Cooling Conditions on Microstructure and Mechanical Properties of Low Carbon Cold Heading Steel |
| LI Zhuang1,2,WU Di2,L�� Wei3 |
1. School of Materials Science and Engineering, Shenyang Aerospace University, Shenyang 110136, Liaoning,China
2. State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110004, Liaoning,China
3. School of Graduate, Shenyang Aerospace University, Shenyang 110136, Liaoning, China |
|
|
|
|
Abstract Effects of rolling and cooling conditions on microstructure and mechanical properties of low carbon cold heading steel were investigated on a laboratory hot rolling mill. The results have shown that the mechanical properties of low carbon steels exceed the standard requirements of ML30, ML35, ML40, and ML45 steel, respectively due to thermomechanical controlled processing (TMCP). This is attributed to a significant amount of pearlite and the ferrite-grain refinement. Under the condition of relatively low temperature rolling, the mechanical properties exceed standard requirements of ML45 and ML30 steel after water cooling and air cooling, respectively. Fast cooling which leads to more pearlite and finer ferrite grains is more critical than finish rolling temperatures for low carbon cold heading steel. The specimen at high finish rolling temperature exhibits very good mechanical properties due to fast cooling. This result has great significance not only for energy saving and emission reduction, but also for low-carbon economy, because the goals of the replacement of medium-carbon by low-carbon are achieved with TMCP.
|
|
Received: 17 August 2011
Published: 28 November 2012
|
| Fund:National Natural Science Foundation of China |
|
Corresponding Authors:
LI Zhuang
E-mail: syli20093@163.com
|
|
|
|
| [1] |
DONG Ze-shang��XUE Qing-guo��ZUO Hai-bin��SHE Xue-feng��WANG Guang��WANG Jing-song. Mathematical model analysis on coke oven gas injection into oxygen blast furnace[J]. Chinese Journal of Iron and Steel, 2017, 52(4): 18-24. |
| [2] |
SUN Yan��kun,ZHANG Wei,,WU Di. Industrial experiment of ultra��fast cooling for large��section bearing steel bar[J]. Chinese Journal of Iron and Steel, 2017, 29(3): 180-184. |
| [3] |
REN Ting-zhi��MA Cai-sheng. Optimization of burden distribution process for blast furnace with bell-less top based on genetic algorithm[J]. Chinese Journal of Iron and Steel, 2016, 51(6): 26-33. |
| [4] |
WANG Zhao-cai��ZHOU Zhi-an��HU Bing��SUN Ying��YE Heng-di��WANG Min. Wind-oxygen balance model of flue gas circulation in sintering[J]. Chinese Journal of Iron and Steel, 2015, 50(12): 53-59. |
| [5] |
HU Bing,, HE Xin-hua,, WANG Zhao-cai,, YE Heng-di,, CHEN Yi-yuan,, SUN Ying,. Wind and Oxygen Balance Based on Flue Gas Circulation Sintering Process[J]. Chinese Journal of Iron and Steel, 2014, 49(9): 15-20. |
| [6] |
LIU Yuan,XU Lei-lei,ZHAO Qing-quan,HE Biao,CAO Jin-rong,XIAO Gong-ye. Effect of Cooling Rate and Cooling Temperature on the Formation of Banded Structure in SA-210Gr. C Steel[J]. Chinese Journal of Iron and Steel, 2014, 26(6): 57-60. |
|
|
|
|
2012, Vol. 19 