| Corrosion Behavior of 110S Tube Steel in Environments of High H2S and CO2 Content |
| LI Wen-fei1,ZHOU Yan-jun1,XUE Yan2 |
1. Drilling Technology Research Institute, Shengli Petroleum Administrative Bureau, Dongying 257017,Shandong, China
2. Xi��an Maurer Petroleum Engineering Laboratory, Xi��an 710065, Shaanxi, China |
|
|
|
|
Abstract The corrosion behavior of the 110S tube steel in the environments of high H2S and CO2 content was investigated by using a high-temperature and high-pressure autoclave, and the corrosion products were characterized by scanning electron microscopy and X-ray diffraction technique. The results showed that all of the corrosion products under the test conditions mainly consisted of different types of iron sulfides such as pyrrhotite of Fe0. 95S, mackinawite of FeS0. 9, Fe0. 985S and FeS, and the absence of iron carbonate in the corrosion scales indicated that the corrosion process was controlled by H2S corrosion. The corrosion rate of the 110S steel decreased firstly and then increased with the rising of temperature. The minimum corrosion rate occurred at 110 ��. When the H2S partial pressure PH2S below 9 MPa, the corrosion rate declined with the increase of PH2S. While over 9 MPa, a higher PH2S resulted in a faster corrosion process. With the increasing of the CO2 partial pressure, the corrosion rate had an increasing trend. The morphologies of the corrosion scales had a good accordance with the corrosion rates.
|
|
Received: 20 September 2011
Published: 27 December 2012
|
| Fund:National Science and Technology Major Project of China |
|
Corresponding Authors:
Jun ZHANG
E-mail: openlab@163.com
|
|
|
|
| [1] |
QIAO Yan-xin,WANG Shuo,GAO Yu-jian,SHI Hong,TANG Rui, XU Fu-jia. Corrosion behavior of ferritic-martensitic steel P92 in supercritical water[J]. Chinese Journal of Iron and Steel, 2016, 28(8): 57-63. |
| [2] |
LI Hao,YANG Cai- fu,CHAI Feng,SU Hang,LUO Xiao- bing. Effect of gas composition on the corrosion behavior of low alloy steel in wet- dry cycling environment[J]. Chinese Journal of Iron and Steel, 2016, 28(1): 50-57. |
| [3] |
LI Hao,,CHAI Feng,HE Yi-zhu,SU Hang,LUO Xiao-bing,ZHAO Jie. Effect of Environment Temperature on Corrosion Behavior of Corrosion Resistant Ship Hull[J]. Chinese Journal of Iron and Steel, 2013, 48(8): 65-69. |
| [4] |
ZHANG Zhi-hong,XUE Xiang-xin,RAN Lian-yu,YANG He,DUAN Pei-ning. Effect of Different Boron Content on Corrosion Resistance of Low Carbon Steel[J]. Chinese Journal of Iron and Steel, 2013, 48(3): 56-59. |
| [5] |
GENG Hong��ming;WU Xiao��chun;MIN Yong��an;WANG Hong��bin;ZHANG Hong��kui. Influence of Copper on Machinability and Corrosion Resistance of 4Cr16Mo Plastic Mould Steel[J]. Chinese Journal of Iron and Steel, 2008, 43(2): 86-0. |
|
|
|
|
2012, Vol. 19 