| Structural Ultrafine Grained Steels Obtained by Advanced Controlled Rolling |
| R Gonz��lez1,J O Garc��a2,M A Barb��s2,M J Quintana1,L F Verdeja2,J I Verdeja2 |
1. School of Engineering, Panamerican University, Mexico City 03920, Mexico
2. E T S I M O, Oviedo University, Oviedo 33004, Spain |
|
|
|
|
Abstract Steels with ultrafine grains (lower than 5 ��m), which usually known as ultrafine ferrite or ultrafine grained materials, are presently the object of intense research, because of the improvement in resistance and fracture toughness they may reach compared to conventional steels (with grain sizes above this value). It is shown that the forenamed steels designated in the Euronorm EN 10149-2, which are manufactured by advanced techniques of controlled rolling and mainly used in automotive industry, have an ultrafine grain size in the range of 2.5 to 3.5 ��m, and with elastic yield stresses higher than 400 MPa. Based on the Morrison-Miller criterion, it is shown that values of the strain-hardening coefficient lower than 0.08 would make the industrial application of these steels unfeasible.
|
|
Received: 11 March 2011
Published: 31 January 2013
|
|
|
|
| [1] |
LI Jun��ZHANG Ling-ling��ZHAO Gui-zhou��CANG Da-qiang. Pilot practice of direct modification of molten blast furnace slag and preparation of mineral wool fiber[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 99-103. |
| [2] |
XU Ren-ze��ZHANG Jian-liang��ZHANG He-shun��LIU Chang-jiang�� FAN Xiao-yue��WANG Zhi-yu. Influence of TiO2 on properties of Jingtang blast furnace slag and thermodynamic analysis[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 104-108. |
| [3] |
JIANG Zhou-hua��ZHANG Xin-fa��LIU Fu-bin��GONG Wei. Harmful impurities control of raw material used in Ni-based superalloy production[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 1-10. |
| [4] |
SONG Guang-yi��YANG Quan��WANG Xiao-chen��ZHANG Xi-bang�� WANG Feng-mei��WANG Qiu-na. Work roll wear law for hot strip temper mill[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 54-59. |
| [5] |
WANG Bing-xing��XIONG Lei��ZHANG Tian��WANG Zhao-dong��WANG Guo-dong. Influence on deformation permeability of plate by controlled rolling process with inter-pass water cooling technology[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 60-65. |
| [6] |
YU Hui��ZHAI Jian-wei��ZHANG Chao-fan��LIU Shuai-shuai��LIU Li-gang. Microstructures and properties of nuclear carbon manganese steels P280GH after accelerated aging[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 66-72. |
|
|
|
|
2013, Vol. 20 