| Anti-Thermal-Fatigue Property of 8407 Steel With Surface Aluminization and Oxidation Treatment |
| SUN Jian1,XU Yu-song1,WANG Xiao-ming2,ZOU Zong-shu2 |
��1. School of Metallurgy and Materials Science, Jiangsu University of Science and Technology Zhangjiagang,Zhangjiagang 215600, Jiangsu, China
2. School of Materials Science and Metallurgy, Northeastern University, Shenyang 110004, Liaoning, China�� |
|
|
|
|
Abstract Thermal fatigue failure is one of the main failure forms of 8407 steel. Aiming at improving the anti-thermal-fatigue property of 8407 steel, the method of aluminization and subsequent oxidation is employed to form a complex oxide on the die surface. Thermal fatigue test was performed with the cycle heating method to compare thermal fatigue behaviors of 8407 steel samples with and without aluminization and oxidation treatment. In the test, thermal fatigue crack morphology formed on the surface was observed by scanning electron microscope (SEM) and then variations of initiating rate and propagating rate of main crack of thermal fatigue with cycles were investigated. Moreover, the thermal fatigue property was judged according to thermal fatigue main crack length and its reciprocal. Finally, the anti-thermal-fatigue mechanism of oxide film was clarified. The results show that the surface aluminization and oxidation treatment can improve both the initiating resistance and propagating resistance of thermal fatigue crack, which will improve the anti-thermal-fatigue property of 8407 steel.
|
|
Received: 22 August 2011
Published: 31 January 2013
|
|
|
|
| [1] |
LI Xin-yu����YANG Mao-sheng��ZHOU Xiao-long��GUO Jun��. Torsion fatigue characteristics and crackpropagation behavior of 15Cr14Co12Mo5Ni2 gear steel[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 84-91. |
| [2] |
LIU Bin,,WU Run,WANG Meng,LIANG Wen,LIU Dong,ZHOU He- rong. Low cycle fatigue properties of hot- rolled high strength dual phase steel[J]. Chinese Journal of Iron and Steel, 2017, 29(8): 667-670. |
| [3] |
LI Yun-ling��ZHONG Zhen-qian. Thermal fatigue crack analysis of the vermicular cast iron brake disc[J]. Chinese Journal of Iron and Steel, 2017, 35(5): 44-46. |
| [4] |
ZHANG Hui-fang��XIAO Zhen-xing��ZHOU Yu��QIAN Li-hua��WANG Wei��[LU]Zhi-qing. Bending fatigue crack initiation and propagation behaviors of a nickel free high nitrogen stainless steel[J]. Chinese Journal of Iron and Steel, 2017, 52(10): 89-93. |
| [5] |
HUANG Ao,,CHEN Ji,ZHANG Xiao-chen,GENG Yue,YANG Bin. Effects of solution treatment on microstructure and fatigue crack propagation behavior of 2205 duplex stainless steel[J]. Chinese Journal of Iron and Steel, 2016, 28(8): 64-68. |
| [6] |
FENG Gang�� ��ZHANG Chao-ge��GONG Da-wei ��HAN Cheng-jiang��LIN Ke-wei��QI Ji-bao��. Closure behavior of fatigue crack by finite element method[J]. Chinese Journal of Iron and Steel, 2016, 51(5): 95-98. |
|
|
|
|
2013, Vol. 20 